Study of air heat treatment on Bi-2223/Ag superconducting tapes

被引：3
作者：
Guo Wei [1 ,2 ,3 ]
Zou Guisheng [1 ,2 ]
Wu Aiping [1 ,2 ]
Wang Yanjun [1 ,2 ]
Bai Hailin [1 ,2 ]
Ren Jialie [1 ,2 ]
机构：
[1] Tsinghua Univ, Dept Mech Engn, Beijing 100084, Peoples R China
[2] Minist Educ PR China, Key Lab Adv Mfg Mat Proc Technol, Beijing 100084, Peoples R China
[3] Beijing Univ Aeronaut & Astronaut, Sch Mech Engn & Automat, Beijing 100191, Peoples R China
来源：
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS | 2009年 / 469卷 / 13期
基金：
中国博士后科学基金; 北京市自然科学基金; 中国国家自然科学基金;
关键词：
Bi-2223/Ag tape; Heat treatment; Critical current; EVOLUTION; TEMPERATURE; TIME;
D O I：
10.1016/j.physc.2009.04.010
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
Heat treatment has been carried out on commercially available Bi-2223/Ag superconducting tape under various temperature conditions in air. The critical currents (I-c) of tape after heat treatment at different annealing temperatures were tested at the liquid-nitrogen temperature. The microstructures and phase constituents of the tapes were investigated by SEM and XRD, respectively. The results indicate that annealing temperature has a very important influence on the superconducting properties of the tapes. When the temperature is above 840 degrees C, I-c value drops dramatically. Furthermore, when the temperature reaches up to 860 degrees C, the tape loses most of its superconducting property because of the decomposition of the superconducting phase Bi-2223. (c) 2009 Elsevier B.V. All rights reserved.
引用
收藏
页码：778 / 781
页数：4
相关论文
共 50 条
  • [41] Ic degradation behaviors of Bi-2223 superconducting tapes under axial fatigue loading
    Shin, HS
    Dizon, JRC
    Kim, KH
    Oh, SS
    Ha, DW
    [J]. CRYOGENICS, 2006, 46 (05) : 378 - 384
  • [42] Comparative studies on "sandwich" rolling and flat rolling in processing Ag/Bi-2223 tapes
    Chen, WM
    Guo, YC
    Fu, XK
    Liu, HK
    Dou, SX
    Apperley, M
    [J]. IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2001, 11 (01) : 3752 - 3755
  • [43] Pinning mechanisms in Bi-2223 tapes with reinforced Ag sheath and oxide additives in the core
    Diantoro, M
    Tjia, MO
    Kovác, P
    Husek, I
    [J]. PHYSICA C, 2001, 357 : 1182 - 1185
  • [44] Critical current of high Tc superconducting Bi2223/Ag tapes
    Huang, YK
    ten Haken, B
    ten Kate, HHJ
    [J]. PHYSICA C, 1998, 309 (3-4): : 197 - 202
  • [45] Physical Effects of Mechanical Processes on Bi-2223 Tapes
    Mustafa Yavuz
    [J]. Journal of Electronic Science and Technology of China, 2008, (02) : 185 - 190
  • [46] Bending strain characteristics of critical current in double-layered Bi-2223 superconducting tapes
    Shin, Hyung-Seop
    Dizon, John R. C.
    Bonifacio, Rolly
    Park, Sung-Taek
    Ha, Dong-Woo
    Oh, Sang-Soo
    [J]. IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2008, 18 (02) : 1155 - 1158
  • [47] A comparison of strain effect on critical current in Bi-2223 superconducting tapes in different bending modes
    Shin, HS
    Choi, SY
    Ko, DK
    Ha, HS
    Ha, DW
    Oh, SS
    [J]. IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2003, 13 (02) : 3526 - 3529
  • [48] Bending strain effects on the critical current of Bi-2223 superconducting tapes by pure bending method
    Lu, Zhaoyangop
    Huang, Xuqiang
    He, Yanfa
    Sun, Jing
    Wang, Jinxing
    [J]. 2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 1975 - +
  • [49] The effect of deformation stress-strain and temperature on the Ic degradation of Bi-2223/Ag tapes
    Ha, Hong-Soo
    Kim, Sang-Cheol
    Ha, Dong-Woo
    Oh, Sang-Soo
    Joo, Jin-Ho
    [J]. PROGRESS IN POWDER METALLURGY, PTS 1 AND 2, 2007, 534-536 : 1609 - +
  • [50] Evidence for enhanced grain connectivity due to second phase reduction of Bi-2223/Ag tapes
    Lehndorff, B
    Hardenbicker, P
    Hortig, M
    Piel, H
    [J]. PHYSICA C, 1999, 312 (1-2): : 105 - 111
12345