Three examples of high-temperature corrosion of metals by molten glasses

被引：11
|
作者：
Rapin, C [1 ]
Vilasi, M [1 ]
Podor, R [1 ]
Carton, A [1 ]
Gaillard-Allemand, B [1 ]
Berthod, P [1 ]
Steinmetz, P [1 ]
机构：
[1] Fac Sci, Lab Chim Solide Mineral, UMR 7555, F-54506 Vandoeuvre Les Nancy, France
来源：
HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 6, PRT 1 AND 2, PROCEEDINGS | 2004年 / 461-464卷
关键词：
corrosion; metal; molten glass; redox; basicity; high-temperature;
D O I：
10.4028/www.scientific.net/MSF.461-464.1125
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effects of glass redox, glass basicity and glass temperature on the metallic material corrosion in molten glass are illustrated with regard to three examples. a) The corrosion of a platinum alloy immersed in a Te-bearing glass under reducing conditions is due to the formation of low melting temperature PtxTe1-x compounds. b) The corrosion of a Ni-base superalloy immersed in a Mo-bearing glass in a reducing atmosphere is due to the dissolution of the chromia protective scale. Indeed the cathodic reaction (Mo(VI)lozenge Mo-III) generates O2- ions which can promote the basic dissolution of Cr2O3. c) The corrosion of a Co-base superalloy in molten C-glass is investigated as a function of temperature, yielding to the demonstration of the existence of a maximum using temperature, characterized by a passive-to-active state transition.
引用
收藏
页码：1125 / 1132
页数：8
相关论文
共 50 条
  • [31] Editorial: Advanced Corrosion Wear Resistant Alloys and their Characterization for High-Temperature Applications
    Xu Liujie
    Ma Shengqiang
    Fu Hanguang
    FRONTIERS IN MATERIALS, 2020, 7 (07):
  • [32] High-temperature corrosion observed in austenitic coils and tubes in a direct reduction process
    B. Campillo
    C. Gonzales
    G. Hernandez-Duque
    J. A. Juarez-Islas
    Journal of Materials Engineering and Performance, 2000, 9 : 88 - 94
  • [33] Thermal Resistance of the Wall Layer of Molten Glass in the High-Temperature Corrosion Zone of the Refractory Walls of the Melting Tank of Glassmaking Furnaces
    Semenov, B. A.
    Ozerov, N. A.
    GLASS AND CERAMICS, 2016, 73 (5-6) : 159 - 164
  • [34] Corrosion resistance of Cr/Ni alloy to a molten carbonate salt at various temperatures for the next generation high-temperature CSP plants
    Encinas-Sanchez, V.
    de Miguel, M. T.
    Garcia-Martin, G.
    Lasanta, M. I.
    Perez, F. J.
    SOLAR ENERGY, 2018, 171 : 286 - 292
  • [35] High-temperature corrosion behavior of zirconia ceramic in molten Na2SO4+NaVO3 salt mixture
    Hui, Yu
    Zhao, Sumei
    Xu, Raying
    Zou, Binglin
    Wang, Ying
    Cai, Xiaolong
    Zhu, Ling
    Cao, Xueqiang
    CERAMICS INTERNATIONAL, 2016, 42 (01) : 341 - 350
  • [36] Thermal Resistance of the Wall Layer of Molten Glass in the High-Temperature Corrosion Zone of the Refractory Walls of the Melting Tank of Glassmaking Furnaces
    B. A. Semenov
    N. A. Ozerov
    Glass and Ceramics, 2016, 73 : 159 - 164
  • [37] Peculiarities of corrosion damage of low alloy chromium on high-temperature salt corrosion
    Rakitskij, A.M.
    Poryadchenko, N.E.
    Panarina, N.I.
    Oryshich, I.V.
    Samelyuk, A.V.
    Fiziko-Khimicheskaya Mekhanika Materialov, 1995, 31 (02): : 103 - 108
  • [38] High-temperature time domain measurement system for solid and molten materials
    Orr, G.
    Ben Ishai, P.
    Roth, M.
    MEASUREMENT SCIENCE AND TECHNOLOGY, 2018, 29 (10)
  • [39] Retardation of High-Temperature Fuel Ash Corrosion of Fireside Boiler Tubes via Nanoparticles
    Khadom, Anees A.
    Liu, Hongfang
    Fadhil, Ahmed A.
    Karim, Abdul Mun'em A.
    OXIDATION OF METALS, 2016, 86 (5-6): : 553 - 565
  • [40] High-temperature corrosion behavior of 316 L stainless steel in carbon dioxide environment
    Chae H.
    Seo S.
    Jung Y.C.
    Lee S.Y.
    Korean J. Mater. Res., 10 (552-556): : 552 - 556
12345