Correlation between Continuous/Discontinuous Yielding and Hall-Petch Slope in High Purity Iron

被引:32
作者
Gao, Si [1 ]
Shibata, Akinobu [1 ]
Chen, Meichuan [1 ]
Park, Nokeun [1 ]
Tsuji, Nobuhiro [1 ]
机构
[1] Kyoto Univ, Dept Mat Sci & Engn, Kyoto 6068501, Japan
关键词
yielding behavior; Hall-Petch relationship; iron; ULTRAFINE-GRAINED ALUMINUM; DEFORMATION; STEELS;
D O I
10.2320/matertrans.MA201326
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
High purity iron specimens containing 11 ppm carbon and 8 ppm nitrogen with different grain sizes were fabricated by cold rolling and subsequent annealing. It was found that the specimens exhibited entirely different yielding behavior in tensile tests depending on different cooling processes after annealing. The water-cooled specimens exhibited continuous yielding while the air-cooled ones exhibited discontinuous yielding. It was found that the Hall-Petch slope, k(y), significantly changed depending on the different yielding behaviors.
引用
收藏
页码:69 / 72
页数:4
相关论文
共 15 条
  • [1] PLASTIC DEFORMATION OF POLYCRYSTALLINE AGGREGATES
    ARMSTRONG, R
    DOUTHWAITE, RM
    CODD, I
    PETCH, NJ
    [J]. PHILOSOPHICAL MAGAZINE, 1962, 7 (73): : 45 - &
  • [2] DISLOCATION THEORY OF YIELDING AND STRAIN AGEING OF IRON
    COTTRELL, AH
    BILBY, BA
    [J]. PROCEEDINGS OF THE PHYSICAL SOCIETY OF LONDON SECTION A, 1949, 62 (349): : 49 - 62
  • [3] Hall E.O., 1970, YIELD POINT PHENOMEN, DOI DOI 10.1007/978-1-4684-1860-6
  • [4] THE DEFORMATION AND AGEING OF MILD STEEL .3. DISCUSSION OF RESULTS
    HALL, EO
    [J]. PROCEEDINGS OF THE PHYSICAL SOCIETY OF LONDON SECTION B, 1951, 64 (381): : 747 - 753
  • [5] KAMIKAWA N, 2005, THESIS OSAKA U
  • [6] Strengthening mechanisms in nanostructured high-purity aluminium deformed to high strain and annealed
    Kamikawa, Naoya
    Huang, Xiaoxu
    Tsuji, Nobuhiro
    Hansen, Niels
    [J]. ACTA MATERIALIA, 2009, 57 (14) : 4198 - 4208
  • [7] Microstructural evolution of IF-steel during cold rolling
    Li, BL
    Godfrey, A
    Meng, QC
    Liu, Q
    Hansen, N
    [J]. ACTA MATERIALIA, 2004, 52 (04) : 1069 - 1081
  • [8] LI CM, 1963, T TMS AIME, V227, P239
  • [9] PETCH NJ, 1953, J IRON STEEL I, V174, P25
  • [10] STRAIN DEPENDENCE OF FLOW STRESS-GRAIN SIZE RELATION FOR 70-30 BRASS
    PHILLIPS, WL
    ARMSTRON.RW
    [J]. METALLURGICAL TRANSACTIONS, 1972, 3 (10): : 2571 - &