Experimental study of vacuum die casting process of AZ91D magnesium alloy

被引：0

作者：

Hu Bo ^{[1
]}

Xiong Shoumei ^{[1
]}

Masayuki Murakami ^{[2
]}

Yoshihide Matsumoto ^{[2
]}

Shingo Ikeda ^{[2
]}

机构：

[1] Tsinghua Univ, Dept Mech Engn, Key Lab Adv Mfg Mat Proc Technol, Beijing 100084, Peoples R China

[2] TOYO Machinery & Met Co Ltd, Tokyo, Japan

来源：

MAGNESIUM TECHNOLOGY 2006, PROCEEDINGS | 2006年

基金：

中国国家自然科学基金;

关键词：

vacuum die casting; magnesium alloy; porosity; and mechanical property;

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The effect of operation conditions in vacuum die casting process on the porosity and mechanical properties of die casting parts of AZ91 alloy were investigated. Standard tensile specimens were cast on a 650t cold chamber die casting machine. Five vacuum levels from 5kpa to 80kpa, as well as the non-vacuum condition, were used and five levels of casting pressure from 22.7MPa to 66.7MPa were applied during the experiments. Other operating conditions were kept constant. Density, tensile strength, yield strength and elongation were measured and relationship between mechanical properties and operating conditions in vacuum die casing were discussed. The results showed that vacuum die casting process of AZ91 magnesium alloy could improve the mechanical properties and reduce the equipment tonnage requirement for the die casting process.

引用

页码：51 / +

页数：2

共 10 条

[1]

*ASTM, 557M02A ASTM B

[2]

*ASTM, 9404 ASTM B

[3]

El-Mahallawy NA, 1998, J MATER PROCESS TECH, V73, P125

[4]

Gjestland H.T., 2004, DIE CASTING ENG, V7, P56

[5]

LIU WH, 2003, 1 INT LIGHT MET TECH, P143

[6]

Liu Z, 2000, METALL, V54, P122

[7] Vacuum assisted high pressure die casting of aluminium alloys [J].

Niu, XP ;

Hu, BH ;

Pinwill, I ;

Li, H .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2000, 105 (1-2) :119-127

[8]

SAKAMOTO T, 2004, DIE CASTING, V76, P283

[9] The effect of die casting machine parameters on porosity of aluminium die castings [J].

Tsoukalas, VD .

INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2003, 15 (06) :581-588

[10]

Wang GG, 2003, MAGNESIUM TECHNOLOGY 2003, P65

← 1 →