Thermal stability of Cr-Cr3Si eutectic microstructures

被引：29
作者：
Gali, A. [1 ,2 ]
Bei, H. [1 ]
George, E. P. [1 ,2 ]
机构：
[1] Oak Ridge Natl Lab, Div Mat Sci & Technol, Oak Ridge, TN 37831 USA
[2] Univ Tennessee, Dept Mat Sci & Engn, Knoxville, TN 37996 USA
来源：
ACTA MATERIALIA | 2009年 / 57卷 / 13期
关键词：
Interfaces; Segregation; Directional solidification; Coarsening; Composites; DIRECTIONAL SOLIDIFICATION; CELLULAR PRECIPITATE; SELF-SIMILARITY; KINETICS; ALLOY; INSTABILITY; SURFACE; GROWTH;
D O I：
10.1016/j.actamat.2009.04.041
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The thermal stability of Cr-Cr3Si lamellar eutectic composites was investigated at temperatures up to 1400 degrees C. In drop-cast Cr-Cr3Si, coarsening was found to be interface controlled. The coarsening rate could be reduced by microalloying with Ce and Re, two elements which were chosen because they were expected to segregate to the Cr-Cr3Si interfaces. Similarly, directional solidification, whichc is also expected to lowere the Cr-Cr3Si interfacial energy, was found to dramatically decrease the coarsening rate. (C) 2009 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：3823 / 3829
页数：7
相关论文
共 31 条
[1]  
ALLEN BC, 1963, T AM SOC MET, V56, P387
[2]   Effects of composition on lamellar microstructures of near-eutectic Cr-Cr3Si alloys [J].
Bei, H ;
George, EP ;
Pharr, GM .
INTERMETALLICS, 2003, 11 (04) :283-289
[3]   Directional solidification and microstructures of near-eutectic Cr-Cr3Si alloys [J].
Bei, H ;
George, EP ;
Kenik, EA ;
Pharr, GM .
ACTA MATERIALIA, 2003, 51 (20) :6241-6252
[4]   EUTECTIC ALLOY SOLIDIFICATION [J].
CHADWICK, GA .
PROGRESS IN MATERIALS SCIENCE, 1963, 12 (02) :99-182
[5]  
CHANG KM, 1992, JOM-J MIN MET MAT S, V44, P59
[6]  
Cruse TA, 1997, 1ST INTERNATIONAL NON-FERROUS PROCESSING AND TECHNOLOGY CONFERENCE, P427
[7]   DISCONTINUOUS COARSENING OF LAMELLAR CELLULAR PRECIPITATE IN AN AUSTENITIC FE-30 WT-PERCENT NI-6 WT-PERCENT TI ALLOY .1. MORPHOLOGY [J].
FOURNELLE, RA .
ACTA METALLURGICA, 1979, 27 (07) :1135-1145
[8]   The structure of interphase boundaries in Al-CuAl2 curved eutectic crystals [J].
Rmong, G.G. ;
Rhodes, C.G. .
Metallurgical and Materials Transactions B: Process Metallurgy and Materials Processing Science, 1974, 5 (12) :2507-2513
[9]   Microstructure and thermal stability of lamellar Cr-silicides [J].
George, EP ;
Bei, H ;
Serin, K ;
Pharr, GM .
THERMEC'2003, PTS 1-5, 2003, 426-4 :4579-4584
[10]  
GRAHAM LD, 1966, T METALL SOC AIME, V236, P94
1234