Measurement of mechanical properties in a 316L stainless steel welded joint

被引：87

作者：

Molak, Rafal M. ^{[1
]}

Paradowski, Krystian ^{[1
]}

Brynk, Tomasz ^{[1
]}

Ciupinski, Lukasz ^{[1
]}

Pakiela, Zbigniew ^{[1
]}

Kurzydlowski, Krzysztof J. ^{[1
]}

机构：

[1] Warsaw Univ Technol, Fac Mat Sci & Engn, PL-02507 Warsaw, Poland

来源：

INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING | 2009年 / 86卷 / 01期

关键词：

Mechanical properties; Welded joints; Microsamples; Digital image correlation; ELECTRON-BEAM; BEHAVIOR;

D O I：

10.1016/j.ijpvp.2008.11.002

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The aim of this study was to measure the mechanical properties of weld material taken from a single weld bead laid down on a 316L steel plate. Due to the low available volume of weld material micro, samples with a total length of 5.5 mm were used. The Digital Image Correlation method (DIC), which enables measurement of mechanical properties of very small samples, was employed for the strain measurements in a uniaxial tensile test. Samples were cut out from three different zones of the specimen: plate, weld, and the heat affected zone. The material from heat affected zone showed the highest value of the Ultimate Tensile Strength (UTS) (580 +/- 7 MPa) and yield strength (339 +/- 6 MPa). Plate material had lower UTS (559 +/- 5 MPa) and yield strength (304 +/- 7 MPa). The lowest values of UTS (526 +/- 6 MPa) and yield strength (291 +/- 8 MPa) have been revealed for the weld. The values obtained for UTS, yield strength and elongation to failure for the plate material were compared with data obtained using standard test specimens. No significant differences between results obtained for the microsamples and standard samples have been found. (C) 2008 Elsevier Ltd. All rights reserved.

引用

页码：43 / 47

页数：5

共 9 条

[1] Digital image correlation used to analyze the multiaxial behavior of rubber-like materials [J].

Chevalier, L ;

Calloch, S ;

Hild, F ;

Marco, Y .

EUROPEAN JOURNAL OF MECHANICS A-SOLIDS, 2001, 20 (02) :169-187

[2] Measured mechanical properties of LIGA Ni structures [J].

Cho, HS ;

Hemker, KJ ;

Lian, K ;

Goettert, J ;

Dirras, G .

SENSORS AND ACTUATORS A-PHYSICAL, 2003, 103 (1-2) :59-63

[3]

*CORR SOL INC, VIC2D SOFTW

[4]

DEQING W, 2004, J MATER SCI, V39, P1689, DOI DOI 10.1023/B:JMSC.0000016171.50107.E4

[5] A study of the heat-affected zone (HAZ) of an Inconel 718 sheet welded with electron-beam welding (EBW) [J].

Huang, CA ;

Wang, TH ;

Lee, CH ;

Han, WC .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 398 (1-2) :275-281

[6] The effect of laser welding process parameters on the mechanical and microstructural properties of V-4Cr-4Ti structural materials [J].

Reed, CB ;

Natesan, K ;

Xu, Z ;

Smith, DL .

JOURNAL OF NUCLEAR MATERIALS, 2000, 283 :1206-1209

[7]

Sus-Ryszkowska M, 2005, SOLID STATE PHENOMEN, V101-102, P85

[8] Microstructural characteristics and creep rupture behavior of electron beam and laser welded AISI 316L stainless steel [J].

Tjong, SC ;

Zhu, SM ;

Ho, NJ ;

Ku, JS .

JOURNAL OF NUCLEAR MATERIALS, 1995, 227 (1-2) :24-31

[9] Microsample tensile testing of nanocrystalline copper [J].

Wang, YM ;

Wang, K ;

Pan, D ;

Lu, K ;

Hemker, KJ ;

Ma, E .

SCRIPTA MATERIALIA, 2003, 48 (12) :1581-1586

← 1 →