Formation of hydrogen blister on AZ91 magnesium alloy during cathodic charging

被引：30

作者：

Chen, Jian ^{[1
]}

Ai, Meirong ^{[1
]}

Wang, Jianqiu ^{[1
]}

Han, En-Hou ^{[1
]}

Ke, Wei ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Liaoning, Peoples R China

来源：

CORROSION SCIENCE | 2009年 / 51卷 / 05期

关键词：

Magnesium; Galvanostatic; STRESS-CORROSION CRACKING; IN-SITU OBSERVATION; MG-AL ALLOY; SODIUM-SULFATE SOLUTION; WET-DRY CONDITIONS; NA2SO4; SOLUTION; BEHAVIOR; INITIATION; HYDRIDE; STEELS;

D O I：

10.1016/j.corsci.2009.02.020

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The process of hydrogen blister formation on as-cast AZ91 magnesium alloy was investigated in 0.1 M NaOH solution using galvanostatic test. The results showed that cathodic charging of AZ91 alloy resulted in hydrogen blister formation, and blister rupture caused the nucleation and propagation of transgranular micro-cracks around the ruptured blister. (C) 2009 Elsevier Ltd. All rights reserved.