Formation of hydrogen blister on AZ91 magnesium alloy during cathodic charging

被引：30

作者：

Chen, Jian ^{[1
]}

Ai, Meirong ^{[1
]}

Wang, Jianqiu ^{[1
]}

Han, En-Hou ^{[1
]}

Ke, Wei ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Liaoning, Peoples R China

来源：

CORROSION SCIENCE | 2009年 / 51卷 / 05期

关键词：

Magnesium; Galvanostatic; STRESS-CORROSION CRACKING; IN-SITU OBSERVATION; MG-AL ALLOY; SODIUM-SULFATE SOLUTION; WET-DRY CONDITIONS; NA2SO4; SOLUTION; BEHAVIOR; INITIATION; HYDRIDE; STEELS;

D O I：

10.1016/j.corsci.2009.02.020

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The process of hydrogen blister formation on as-cast AZ91 magnesium alloy was investigated in 0.1 M NaOH solution using galvanostatic test. The results showed that cathodic charging of AZ91 alloy resulted in hydrogen blister formation, and blister rupture caused the nucleation and propagation of transgranular micro-cracks around the ruptured blister. (C) 2009 Elsevier Ltd. All rights reserved.

引用

页码：1197 / 1200

页数：4

共 25 条

[1] CHLORIDE CORROSION OF AUSTENITIC STAINLESS-STEELS AND OF AN INCONEL ALLOY IN HOT ACIDIC MEDIA [J].

ALI, SI ;

ABBASCHIAN, GJ .

CORROSION SCIENCE, 1978, 18 (01) :15-19

[2] TRANSGRANULAR SCC OF A MG-AL ALLOY - CRYSTALLOGRAPHIC, FRACTOGRAPHIC AND ACOUSTIC-EMISSION STUDIES [J].

CHAKRAPANI, DG ;

PUGH, EN .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1975, 6 (06) :1155-1163

[3] HYDROGEN EMBRITTLEMENT IN A MG-AL ALLOY [J].

CHAKRAPANI, DG ;

PUGH, EN .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1976, 7 (02) :173-178

[4] FRACTOGRAPHY OF TRANSGRANULAR STRESS-CORROSION FAILURES IN A MG-AL ALLOY [J].

CHAKRAPANI, DG ;

PUGH, EN .

CORROSION, 1975, 31 (07) :247-252

[5] In Situ Observation of Initial Corrosion of MgAl9Zn1 Magnesium Alloy in Cyclic Wet-Dry Conditions Using Environmental Scanning Electron Microscopy [J].

Chen, J. ;

Wang, J. ;

Han, E. ;

Ke, W. .

CORROSION, 2007, 63 (07) :661-671

[6] Corrosion behavior of AZ91D magnesium alloy in sodium sulfate solution [J].

Chen, J. ;

Wang, J. ;

Han, E. ;

Dong, J. ;

Ke, W. .

MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2006, 57 (10) :789-793

[7] In situ observation of crack initiation and propagation of the charged magnesium alloy under cyclic wet-dry conditions [J].

Chen, Jian ;

Wang, Jianqiu ;

Han, Enhou ;

Ke, Wei .

CORROSION SCIENCE, 2008, 50 (08) :2338-2341

[8] Electrochemical corrosion and mechanical behaviors of the charged magnesium [J].

Chen, Jian ;

Wang, Jianqiu ;

Han, Enhou ;

Ke, Wei .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 494 (1-2) :257-262

[9] Effect of hydrogen on stress corrosion cracking of magnesium alloy in 0.1 M Na2SO4 solution [J].

Chen, Jian ;

Wang, Jianqiu ;

Han, Enhou ;

Ke, Wei .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 488 (1-2) :428-434

[10] States and transport of hydrogen in the corrosion process of an AZ91 magnesium alloy in aqueous solution [J].

Chen, Jian ;

Wang, Jianqiu ;

Han, Enhou ;

Dong, Junhua ;

Ke, Wei .

CORROSION SCIENCE, 2008, 50 (05) :1292-1305

← 1 2 3 →