Effect of post weld heat treatment on weldability of high entropy alloy welds

The effect of post weld heat treatment (PWHT) temperature on laser beam welds in high-entropy alloys (HEAs) using a cold-rolled cantor system (CoCrFeMnNi) was investigated. Laser welding of low heat input was applied to reduce thermal distortion. The cold-rolled HEA welds indicated larger grain size and inferior tensile/hardness properties as compared to the base metal (BM). By applying PWHT, the welds showed superior hardness to the BM with no variation in the face-centred cubic phase and a decrease in the size and fraction of CrMn oxide inclusions. As the PWHT temperature increased (800-1000 degrees C), the variation in the grain size decreased between the weld metal and heat-affected zone, thus resulting in approximately the same tensile strength and elongation of the transverse welds as compared to the BM.