Continuous cooling precipitation diagram of high alloyed Al-Zn-Mg-Cu 7049A alloy

被引：14
作者：
Zohrabyan, Davit [1 ,2 ]
Milkereit, Benjamin [1 ,2 ]
Schick, Christoph [2 ]
Kessler, Olaf [1 ]
机构：
[1] Univ Rostock, Chair Mat Sci, D-18051 Rostock, Germany
[2] Univ Rostock, Polymer Phys Grp, D-18051 Rostock, Germany
来源：
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2014年 / 24卷 / 07期
关键词：
differential scanning calorimetry (DSC); differential fast scanning calorimetry (DFSC); 7049A alloy; differential reheating method; continuous cooling precipitation; ALUMINUM-ALLOYS; QUENCH SENSITIVITY; CCT DIAGRAM; MICROSTRUCTURE;
D O I：
10.1016/S1003-6326(14)63307-0
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The precipitation behaviour during cooling from solution annealing of high alloyed 7049A aluminium alloy was investigated, covering the complete cooling-rate-range of technical interest. This ranges from slow cooling rates close to equilibrium up to rates above complete supersaturation and is covering seven orders of magnitude in cooling rate (0.0005 to 5000 K/s). The continuous cooling precipitation behaviour of 7049A alloy was recorded by combining different differential scanning calorimetry (DSC) techniques and microstructure analysis by SEM and Vickers hardness testing. The high alloyed, high strength and quench sensitive wrought aluminium alloy 7049A was investigated during quenching from solution annealing by conventional DSC in the cooling rate range of 0.0005 to 4 K/s. In this range at least two exothermal precipitation reactions were observed: a high temperature reaction in a narrow temperature interval of 450-430 degrees C, and a low temperature reaction in a broad temperature interval down to about 200 degrees C. Intensities of both reactions decreased with increasing cooling rate. Quenching from solution annealing with rates up to 1000 K/s was investigated by differential fast scanning calorimetry (DFSC) and the differential reheating method (DRM). A critical quenching rate to suppress all precipitation reactions of 100-300 K/s was been determined.
引用
收藏
页码：2018 / 2024
页数：7
相关论文
共 20 条
  • [11] The continuous cooling precipitation diagram of an aluminum alloy EN AW-6005A
    Milkereit, B.
    Jonas, L.
    Schick, C.
    Kessler, O.
    [J]. HTM-JOURNAL OF HEAT TREATMENT AND MATERIALS, 2010, 65 (03): : 159 - 171
  • [12] Continuous cooling precipitation diagrams of Al-Mg-Si alloys
    Milkereit, Benjamin
    Wanderka, Nelia
    Schick, Christoph
    Kessler, Olaf
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 550 : 87 - 96
  • [13] Precipitation kinetics of an aluminium alloy during Newtonian cooling simulated in a differential scanning calorimeter
    Milkereit, Benjamin
    Beck, Martin
    Reich, Michael
    Kessler, Olaf
    Schick, Christoph
    [J]. THERMOCHIMICA ACTA, 2011, 522 (1-2) : 86 - 95
  • [14] Recording of continuous cooling precipitation diagrams of aluminium alloys
    Milkereit, Benjamin
    Kessler, Olaf
    Schick, Christoph
    [J]. THERMOCHIMICA ACTA, 2009, 492 (1-2) : 73 - 78
  • [15] Ultrafast thermal processing and nanocalorimetry at heating and cooling rates up to 1 MK/s
    Minakov, Alexander A.
    Schick, Christoph
    [J]. REVIEW OF SCIENTIFIC INSTRUMENTS, 2007, 78 (07)
  • [16] Polmear I., 2006, LIGHT ALLOYS, V4th
  • [17] von BARGEN R, 2002, HTM J HEAT TREATMENT, V62, P285
  • [18] Zajac S., 2000, INT AL EXTR TECHN SE, P73
  • [19] Fast scanning power compensated differential scanning nano-calorimeter: 1. The device
    Zhuravlev, E.
    Schick, C.
    [J]. THERMOCHIMICA ACTA, 2010, 505 (1-2) : 1 - 13
  • [20] Precipitation enthalpy during cooling of aluminum alloys obtained from calorimetric reheating experiments
    Zohrabyan, Davit
    Milkereit, Benjamin
    Kessler, Olaf
    Schick, Christoph
    [J]. THERMOCHIMICA ACTA, 2012, 529 : 51 - 58
12