Microstructure and properties of spark plasma-sintered ZrO2-ZrB2 nanoceramic composites

被引:42
作者
Basu, Bikramjit [1 ]
Venkateswaran, T.
Kim, Doh-Yeon
机构
[1] Indian Inst Technol, Dept Mat & Met Engn, Lab Adv Ceram, Kanpur 208016, Uttar Pradesh, India
[2] Seoul Natl Univ, Sch Mat Sci & Engn, Seoul 151744, South Korea
[3] Seoul Natl Univ, Ctr Microstruct Sci Mat, Seoul 151744, South Korea
关键词
D O I
10.1111/j.1551-2916.2006.01083.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
In a recent work,(1) we have reported the optimization of the spark plasma sintering (SPS) parameters to obtain dense nanostructured 3Y-TZP ceramics. Following this, the present work attempts to answer some specific issues: (a) whether ZrO2-based composites with ZrB2 reinforcements can be densified under the optimal SPS conditions for TZP matrix densification (b) whether improved hardness can be obtained in the composites, when 30 vol% ZrB2 is incorporated and (c) whether the toughness can be tailored by varying the ZrO2-matrix stabilization as well as retaining finer ZrO2 grains. In the present contribution, the SPS experiments are carried out at 1200 degrees C for 5 min under vacuum at a heating rate of 600 K/min. The SPS processing route enables retaining of the finer t-ZrO2 grains (100-300 nm) and the ZrO2-ZrB2 composite developed exhibits optimum hardness up to 14 GPa. Careful analysis of the indentation data provides a range of toughness values in the composites (up to 11 MPa.m(1/2)), based on Y2O3 stabilization in the ZrO2 matrix. The influence of varying yttria content, t-ZrO2 transformability, and microstructure on the properties obtained is discussed. In addition to active contribution from the transformation-toughening mechanism, crack deflection by hard second phase brings about appreciable increment in the toughness of the nanocomposites.
引用
收藏
页码:2405 / 2412
页数:8
相关论文
共 34 条
  • [31] INDENTATION FRACTURE OF WC-CO CERMETS
    SHETTY, DK
    WRIGHT, IG
    MINCER, PN
    CLAUER, AH
    [J]. JOURNAL OF MATERIALS SCIENCE, 1985, 20 (05) : 1873 - 1882
  • [32] TORAYA H, 1984, J AM CERAM SOC, V67, pC119, DOI 10.1111/j.1151-2916.1984.tb19715.x
  • [33] Modelling of the temperature distribution during field assisted sintering
    Vanmeensel, K
    Laptev, A
    Hennicke, J
    Vleugels, J
    Van der Biest, O
    [J]. ACTA MATERIALIA, 2005, 53 (16) : 4379 - 4388
  • [34] WATCHMAN JB, MECH PROPERTIES CERA, P391