Spot friction stir welding of low carbon steel plates preheated by high frequency induction

被引：59
作者：
Sun, Y. F. [1 ]
Shen, J. M. [1 ]
Morisada, Y. [1 ]
Fujii, H. [1 ]
机构：
[1] Osaka Univ, Joining & Welding Res Inst, Ibaraki, Japan
来源：
MATERIALS & DESIGN | 2014年 / 54卷
基金：
日本科学技术振兴机构;
关键词：
Spot friction stir welding; Preheating; Shear tensile test; MECHANICAL-PROPERTIES; ALLOY TOOL; MICROSTRUCTURE; SPEED;
D O I：
10.1016/j.matdes.2013.08.071
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this study, high frequency induction heating assisted spot friction stir welding was applied to 1.6 mm thick S12C low carbon steel plates. With the same welding parameter including an applied load of 2500 kg, rotation speed of 800 rpm and dwell time of 2 s, the average grain size in the stir zone slightly increased from 12.9 mu m for the welds without preheating to 14.8 mu m when 10 s preheating was used. However, larger joint interface was formed within the stir zone of the welds with preheating and therefore the bonding strength can be significantly increased. As a result, the shear tensile load of the joint increased from 8 kN to 12.4 kN with preheating and the joint fractured through the plug failure mode rather than interfacial failure mode. It was revealed that the frictional heat generated between the rotating tool and the work-piece can be reduced to obtain sound welds by means of high frequency induction preheating. (C) 2013 Elsevier Ltd. All rights reserved.
引用
收藏
页码：450 / 457
页数：8
相关论文
共 32 条
[1]  
[Anonymous], 2005, SAE T
[2]  
[Anonymous], P 6 INT S FRICT STIR
[3]  
[Anonymous], 2001, P 3 INT S FRICT STIR
[4]  
[Anonymous], 1999, Z3136 JIS, P305
[5]  
Aota K, 2004, [No title captured], Patent No. [EP1430986, 1430986]
[6]   Structure-Properties Relations in Friction Stir Spot Welded Low Carbon Steel Sheets for Light Weight Automobile Body [J].
Baek, Seung-Wook ;
Choi, Don-Hyun ;
Lee, Chang-Yong ;
Ahn, Byung-Wook ;
Yeon, Yun-Mo ;
Song, Keun ;
Jung, Seung-Boo .
MATERIALS TRANSACTIONS, 2010, 51 (02) :399-403
[7]   Frictional wear evaluation of WC-Co alloy tool in friction stir spot welding of low carbon steel plates [J].
Choi, D. H. ;
Lee, C. Y. ;
Ahn, B. W. ;
Choi, J. H. ;
Yeon, Y. M. ;
Song, K. ;
Park, H. S. ;
Kim, Y. J. ;
Yoo, C. D. ;
Jung, S. B. .
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2009, 27 (06) :931-936
[8]   Grade development of polycrystalline cubic boron nitride for friction stir processing of ferrous alloys [J].
Collier, M ;
Steel, R ;
Nelson, T ;
Sorensen, C ;
Packer, S .
THERMEC'2003, PTS 1-5, 2003, 426-4 :3011-3016
[9]   The origin of non-uniform microstructure and its effects on the mechanical properties of a friction stir processed Al-Mg alloy [J].
Cui, G. R. ;
Ma, Z. Y. ;
Li, S. X. .
ACTA MATERIALIA, 2009, 57 (19) :5718-5729
[10]   Friction stir welding of a high carbon steel [J].
Cui, Ling ;
Fujii, Hidetoshi ;
Tsuji, Nobuhiro ;
Nogi, Kiyoshi .
SCRIPTA MATERIALIA, 2007, 56 (07) :637-640
1234