Effects of oxide thickness, Al2O3 interlayer and interface asperity on residual stresses in thermal barrier coatings

被引：30

作者：

Zhang, X. C. ^{[1
]}

Xu, B. S.

Wang, H. D.

Wu, Y. X.

机构：

[1] Shanghai Jiao Tong Univ, State Key Lab Met Matrix Composites, Shanghai 200030, Peoples R China

[2] Natl Key Lab Reanufacturing, Beijing 100072, Peoples R China

来源：

MATERIALS & DESIGN | 2006年 / 27卷 / 10期

关键词：

thermal barrier coatings; residual stress; concentric-circle model; thermally grown oxide; finite element method;

D O I：

10.1016/j.matdes.2005.02.008

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

During high temperature operation, the thermally grown oxide (TGO) usually forms along the bondcoat/topcoat interface in thermal barrier coating (TBC) and was characterized as a driving force for the failure of the coating system. The effects of TGO thickness and Al2O3 interlayer applied as an oxygen barrier layer between the bondcoat and topcoat on the magnitude of residual stresses in TBC during cooling process were interpreted using concentric-circle model. The results were coupled with finite element method. The influences of interface asperity and interface topography on the distribution of residual stresses normal to interfaces in TBC were also discussed. (C) 2005 Elsevier Ltd. All rights reserved.

引用

页码：989 / 996

页数：8

共 15 条

[11] Experimental and analytical evaluation of damage processes in thermal barrier coatings [J].

Nusier, SQ ;

Newaz, GM ;

Chaudhury, ZA .

INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2000, 37 (18) :2495-2506

[12] Materials science - Thermal barrier coatings for gas-turbine engine applications [J].

Padture, NP ;

Gell, M ;

Jordan, EH .

SCIENCE, 2002, 296 (5566) :280-284

[13] The effect of interface roughness and oxide film thickness on the inelastic response of thermal barrier coatings to thermal cycling [J].

Pindera, MJ ;

Aboudi, J ;

Arnold, SM .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 284 (1-2) :158-175

[14] Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings [J].

Rabiei, A ;

Evans, AG .

ACTA MATERIALIA, 2000, 48 (15) :3963-3976

[15]

Timoshenko S, 1976, STRENGTH MAT 2

← 1 2 →