Bond characteristics of carbon fabric-reinforced cementitious matrix in double shear tests

被引：50

作者：

Awani, Oluwafunmilayo ^{[1
]}

El Refai, Ahmed ^{[2
]}

El-Maaddawy, Tamer ^{[1
]}

机构：

[1] United Arab Emirates Univ, Dept Civil & Environm Engn, Al Ain, U Arab Emirates

[2] Univ Laval, Dept Civil & Water Engn, Quebec City, PQ G1V 0A6, Canada

来源：

CONSTRUCTION AND BUILDING MATERIALS | 2015年 / 101卷

关键词：

Bond; Cementitious matrix; Concrete; Double shear; FRCM; Fabric; Fiber; Mortars; Textile; TRM; TENSILE BEHAVIOR; CONCRETE BEAMS; FRCM MATERIALS; DURABILITY;

D O I：

10.1016/j.conbuildmat.2015.10.017

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

This study examined the bond characteristics between fabric-reinforced cementitious matrix (FRCM) systems and concrete. Twenty-seven double-shear specimens were tested under direct shear loading. Two types of cementitious mortars (FRCM specimens) and one type of epoxy (FRE specimens) were used as a matrix. Fabric delamination governed the failure of the FRCM specimens without debonding at the concrete/matrix interface. The FRCM specimens experienced cracking prior to failure whereas the FRE specimens failed suddenly by fabric rupture without cracking. The bond stress of the FRCM specimens at failure was on average 28% lower than that of the FRE specimens. For the same width of the bonded area, the bond stress at failure typically decreased with an increase in the bonded length of the fabric. Similarly, for the same bonded area, the bond stress at failure tended to decrease by increasing the bonded length. This reduction in the bond stress at failure was more pronounced in the FRE specimens than in the FRCM specimens. (C) 2015 Elsevier Ltd. All rights reserved.

引用

页码：39 / 49

页数：11

共 29 条

[1] Experimental and Numerical Study for the Shear Strengthening of Reinforced Concrete Beams Using Textile-Reinforced Mortar [J].

Al-Salloum, Yousef A. ;

Elsanadedy, Hussein M. ;

Alsayed, Saleh H. ;

Iqbal, Rizwan A. .

JOURNAL OF COMPOSITES FOR CONSTRUCTION, 2012, 16 (01) :74-90

[2]

[Anonymous], 2007, INT C ADV COMP CONST

[3]

[Anonymous], 2013, 5494R13 ACI COMM

[4]

Bissonnette B., 2012, 1217 MERL US DEP INT

[5] Shear creep of epoxy at the concrete-FRP interfaces [J].

Choi, Kyoung-Kyu ;

Meshgin, Pania ;

Taha, Mahmoud M. Reda .

COMPOSITES PART B-ENGINEERING, 2007, 38 (5-6) :772-780

[6] Textile Reinforced Concrete: experimental investigation on design parameters [J].

Colombo, Isabella Giorgia ;

Magri, Anna ;

Zani, Giulio ;

Colombo, Matteo ;

di Prisco, Marco .

MATERIALS AND STRUCTURES, 2013, 46 (11) :1933-1951

[7] Contribution to direct tensile testing of textile reinforced concrete (TRC) composites [J].

Contamine, R. ;

Larbi, A. Si ;

Hamelin, P. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (29-30) :8589-8598

[8] Tensile and in-plane shear behaviour of textile reinforced concrete: Analysis of a new multiscale reinforcement [J].

Contamine, Raphael ;

Junes, Angel ;

Larbi, Amir Si .

CONSTRUCTION AND BUILDING MATERIALS, 2014, 51 :405-413

[9] Experimental and analytical investigation on bond between Carbon-FRCM materials and masonry [J].

D'Ambrisi, Angelo ;

Feo, Luciano ;

Focacci, Francesco .

COMPOSITES PART B-ENGINEERING, 2013, 46 :15-20

[10] Bond-slip relations for PBO-FRCM materials externally bonded to concrete [J].

D'Ambrisi, Angelo ;

Feo, Luciano ;

Focacci, Francesco .

COMPOSITES PART B-ENGINEERING, 2012, 43 (08) :2938-2949

← 1 2 3 →