Processing Li2O-Al2O3-SiO2 (LAS) glass-ceramic with and without P2O5 through bulk and sintering route

被引：26

作者：

Venkateswaran, C. ^{[1
]}

Sreemoolanadhan, H. ^{[1
]}

Pant, Bhanu ^{[1
]}

Sharma, S. C. ^{[1
]}

Chauhan, V. S. ^{[2
]}

Vaish, Rahul ^{[2
]}

机构：

[1] ISRO, Vikram Sarabhai Space Ctr, Thiruvananthapuram, Kerala, India

[2] Indian Inst Technol, Sch Engn, Mandi, Himachal Prades, India

来源：

JOURNAL OF NON-CRYSTALLINE SOLIDS | 2020年 / 550卷

关键词：

Low thermal expansion; Negative thermal expansion; Lithium aluminosilicate; Glass-ceramics; LITHIUM ALUMINOSILICATE GLASS; ZERO THERMAL-EXPANSION; HOMOGENEOUS NUCLEATION; TIO2; CONTENT; CRYSTALLIZATION; SILICATE; TEMPERATURE; PHOSPHORUS; VISCOSITY; COLOR;

D O I：

10.1016/j.jnoncrysol.2020.120289

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Commercially significant Li2O-Al2O3-SiO2 (LAS) glass composition with P2O5 content varying between 0 - 6.8 mol% were prepared through the conventional melt-quenching route. From high-temperature dilation results, it was found that different amount of P2O5 in the LAS glass greatly influences the phase transformation (glass transition, softening and melting) characteristics. Two LAS glass systems, namely 3.1 mol% of P2O5 (P3.1) and without P2O5 (P0) were considered further towards making low expansion glass-ceramic using bulk and sin tering route due to their contrary thermal behaviour. The optimum nucleation temperature for P0 and P3.1 glass system was determined to be 640 and 700 degrees C, respectively using the Marotta method. Effect of heat-treatment temperature on the thermal expansion behaviours of the LAS glass-ceramic is explained in detail. Negative thermal expansion (NTE) and low expansion glass-ceramics were produced from bulk and sintering route. Transparent beta-quartz s.s. based ultra-low thermal expansion (0.04 x10(-6) degrees C-1 between -60 degrees C and 400 degrees C) glassceramic was produced.

引用

页数：11

共 38 条

[31] Effect of P2O5 on the Nonisothermal Sinter-Crystallization Process of a Lithium Aluminum Silicate Glass [J].

Soares, Viviane Oliveira ;

Zanotto, Edgar Dutra .

INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2016, 13 (05) :948-955

[32] The variable influence of P2O5 on the viscosity of melts of differing alkali/aluminium ratio: Implications for the structural role of phosphorus in silicate melts [J].

Toplis, MJ ;

Dingwell, DB .

GEOCHIMICA ET COSMOCHIMICA ACTA, 1996, 60 (21) :4107-4121

[33] Crystallisation studies on site saturated lithium aluminosilicate (LAS) glass [J].

Venkateswaran, C. ;

Sharma, S. C. ;

Pant, Bhanu ;

Chauhan, V. S. ;

Vaish, Rahul .

THERMOCHIMICA ACTA, 2019, 679

[34] Near-zero thermal expansion transparent lithium aluminosilicate glass-ceramic by microwave hybrid heat treatment [J].

Venkateswaran, C. ;

Sharma, Sharad C. ;

Chauhan, Vishal S. ;

Vaish, Rahul .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2018, 101 (01) :140-150

[35] The effect of complex nucleating agent on the crystallization, phase formation and performances in lithium aluminum silicate (LAS) glasses [J].

Wu, Jiaqi ;

Lin, Changwei ;

Liu, Jianlei ;

Han, Lei ;

Gui, Hua ;

Li, Cui ;

Liu, Taoyong ;

Lu, Anxian .

JOURNAL OF NON-CRYSTALLINE SOLIDS, 2019, 521

[36] Effects of B2O3 and P2O5 doping on the microstructure evolution and mechanical strength in a lithium aluminosilicate glass ceramic material with TiO2 and ZrO2 [J].

Wu, Yu-Han ;

Hsu, Kuo-Chuan ;

Lee, Chih-Hao .

CERAMICS INTERNATIONAL, 2012, 38 (05) :4111-4121

[37] Crystal growth in a multicomponent lithia aluminosilicate glass [J].

Wurth, R. ;

Munoz, F. ;

Mueller, M. ;

Ruessel, C. .

MATERIALS CHEMISTRY AND PHYSICS, 2009, 116 (2-3) :433-437

[38] Preparation and thermal properties of P2O5 doped Li2O-Al2O3-SiO2 glass-ceramics [J].

Xiao, Zhuohao ;

Zhou, Jianer ;

Luo, Wenyan .

ADVANCES IN SUPERALLOYS, PTS 1 AND 2, 2011, 146-147 :1574-1577

← 1 2 3 4 →