Microstructure and mechanical properties of dual-phase weathering steel 09CuPTiRe

被引：10
|
作者：
Zhang, CL [1 ]
Cai, DY
Liao, B
Zhao, TC
Fan, YC
机构：
[1] Yanshan Univ, Key Lab Mestastable Mat Sci & Technol, Qinhuangdao 066004, Peoples R China
[2] Shijiazhuang Rail Inst, Dept Mat Sci & Engn, Shijiazhuang 050043, Peoples R China
来源：
JOURNAL OF MATERIALS SCIENCE | 2004年 / 39卷 / 13期
关键词：
Copper alloys - Corrosion resistance - Ductility - Ferrite - Formability - Heat treatment - Martensite - Microstructure - Optical microscopy - Steel construction - Strength of materials - Tensile strength - Transmission electron microscopy - Weathering - X ray diffraction;
D O I：
10.1023/B:JMSC.0000033436.06575.aa
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The microstructure and mechanical properties of dual-phase weathering steel 09CuPtRe were analyzed. Tensile tests on an INSTRON machine with a speed of 0.5 mm/min were conducted and microstructure observations were carried out. It was observed that martensite islands randomly get distributed and the volume of martensite increased with the increase of quenching temperature. It was found that a successful dual-phase 09CuPTiRe steel with excellent formability qualities was obtained through intercritical quenching at 780°.
引用
收藏
页码：4393 / 4396
页数：4
相关论文
共 50 条
  • [31] Effect of Quenching in Dual-phase Region on Microstructure and Mechanical Properties of 7Ni Steel
    Xu Li-xiong
    Wu Hui-bin
    Mou Dan
    CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2018, 46 (08): : 113 - 119
  • [32] Effect of holding time on the microstructure and mechanical properties of dual-phase steel during intercritical annealing
    Zhuang Li
    Di Wu
    Wei Lü
    Huanhuan Yu
    Zhenyao Shao
    Lei Luo
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2015, 30 : 156 - 161
  • [33] Effect of Intercritical Temperature on the Microstructure and Mechanical Properties of 10CrMnMoSi Dual-phase Steel
    Zhou, Peishan
    Wang, Liang
    Cui, Chengwu
    Hu, Yiwen
    Xu, Kailiang
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (19) : 8949 - 8960
  • [34] Microstructure Evolution and Mechanical Properties of 780 MPa Hot Dip Galvanized Dual-Phase Steel
    Li, Guo Bin
    Zhao, Zheng Zhi
    Tang, Di
    ADVANCES IN SUPERALLOYS, PTS 1 AND 2, 2011, 146-147 : 1331 - +
  • [35] The Prediction of the Mechanical Properties for Dual-Phase High Strength Steel Grades Based on Microstructure Characteristics
    Evin, Emil
    Kepic, Jan
    Burikova, Katarina
    Tomas, Miroslav
    METALS, 2018, 8 (04):
  • [36] Effect of Holding Time on the Microstructure and Mechanical Properties of Dual-Phase Steel during Intercritical Annealing
    Li Zhuang
    Wu Di
    Lu Wei
    Yu Huanhuan
    Shao Zhenyao
    Luo Lei
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2015, 30 (01): : 156 - 161
  • [37] MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF A QUENCHED AND TEMPERED CR-V DUAL-PHASE STEEL
    SAMUEL, FH
    HUSSEIN, AA
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1983, 23 (03) : 213 - 217
  • [38] Effect of Ferrite/Martensite on Microstructure Evolution and Mechanical Properties of Ultrafine Vanadium Dual-Phase Steel
    Bilal Nawaz
    Xiaoyan Long
    Yanguo Li
    Zhinan Yang
    Fucheng Zhang
    Journal of Materials Engineering and Performance, 2022, 31 : 4305 - 4317
  • [39] Effect of intercritical annealing on the mechanical properties of dual-phase steel
    Ayres, James
    Penney, David
    Evans, Peter
    Underhill, Richard
    IRONMAKING & STEELMAKING, 2022, 49 (08) : 821 - 827
  • [40] Mechanical properties of dual-phase steel with long, fibrous martensite
    Sun, S
    Pugh, M
    METAL WELDING AND APPLICATIONS: THERMOMECHANICAL PROCESSING OF ALLOYS, 1999, : 439 - 448
12345