Sintering kinetics of submicron sized cobalt powder

被引：15

作者：

Paul, Bhaskar ^{[2
]}

Jain, Dheeraj ^{[1
]}

Bidaye, A. C. ^{[2
]}

Sharma, I. G. ^{[2
]}

Pillai, C. G. S. ^{[1
]}

机构：

[1] Bhabha Atom Res Ctr, Div Chem, Bombay 400085, Maharashtra, India

[2] Bhabha Atom Res Ctr, Mat Proc Div, Bombay 400085, Maharashtra, India

来源：

THERMOCHIMICA ACTA | 2009年 / 488卷 / 1-2期

关键词：

Sintering; Kinetics; Cobalt; Dilatometry; SID; AMMONIA CRACKER CATALYST; HIGH-PURITY COBALT; NICKEL; IRON;

D O I：

10.1016/j.tca.2009.01.017

中图分类号：

O414.1 [热力学];

学科分类号：

摘要：

The paper details the results of sintering kinetics studies on submicron sized fine cobalt metal powders prepared through oxalate decomposition route using both conventional sintering method as well as stepwise isothermal dilatometry (SID) technique. Powder preparation and processing parameters such as decomposition temperature, compaction pressure and sintering atmosphere, etc. were optimized to achieve highest sintered density with lowest activation energy through conventional sintering. Role of submicron sized powder and surface contamination layers on initial shrinkage was explained towards early shrinkage of cobalt compacts by dilatometric analysis. Measured step isothermal shrinkage data were analyzed by Makipirtti-Meng method. The shrinkage data were found to fit well with the rate equation proposed in this method and its validity was established for the metallic systems also. Kinetic parameters were evaluated and sintering was found to occur through three major mechanisms operative successively, which are grain boundary diffusion, lattice diffusion and plastic/viscous flow with the energy of activation as 135, 234 and 373 kJ/mol, respectively. The results were well supported by microstructural analysis of sintered specimens. (C) 2009 Elsevier B.V. All rights reserved.

引用

页码：54 / 59

页数：6

共 16 条

[1] Initial sintering kinetics of attrition milled nanocrystalline titanium powders [J].

Dabhade, V. V. ;

Mohan, T. R. Rama ;

Ramakrishnan, P. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 452 :386-394

[2] Material transport mechanisms and activation energy in nanometric Fe powders based on sintering experiments [J].

Dominguez, O ;

Bigot, J .

NANOSTRUCTURED MATERIALS, 1995, 6 (5-8) :877-880

[3]

GERMAN RM, 1994, POWDER METALLURGY SC, P250

[4] SINTERING DIAGRAMS FOR COBALT, NICKEL AND IRON [J].

JERNOT, JP ;

CHERMANT, JL ;

DESCHANVRES, A ;

MORDIKE, BL .

MATERIALS RESEARCH BULLETIN, 1982, 17 (06) :815-822

[5] Micro powder injection molding: Sintering kinetics of microstructured components [J].

Liu, L. ;

Loh, N. H. ;

Tay, B. Y. ;

Tor, S. B. ;

Murakoshi, Y. ;

Maeda, R. .

SCRIPTA MATERIALIA, 2006, 55 (12) :1103-1106

[6] Kinetics of the reactive sintering of kaolinite-aluminum hydroxide extrudate [J].

Liu, YF ;

Liu, XQ ;

Tao, SW ;

Meng, GY ;

Sorensen, OT .

CERAMICS INTERNATIONAL, 2002, 28 (05) :479-486

[7]

Meng G., 1991, ADV STRUCTURAL MAT, V2, P369

[8] Hot working characteristics of cobalt in the temperature range 600-950 °C [J].

Paul, B. ;

Kapoor, R. ;

Chakravartty, J. K. ;

Bidaye, A. C. ;

Sharma, I. G. ;

Suri, A. K. .

SCRIPTA MATERIALIA, 2009, 60 (02) :104-107

[9] Recovery of high purity cobalt from spent ammonia cracker catalyst [J].

Rane, MV ;

Bafna, VH ;

Sadanandam, R ;

Sharma, AK ;

Ramadevi, K ;

Menon, NK ;

Fonseca, MF ;

Tangri, SK ;

Suri, AK .

HYDROMETALLURGY, 2005, 77 (3-4) :247-251

[10] Production of high purity cobalt oxalate from spent ammonia cracker catalyst [J].

Sadanandam, R. ;

Fonseca, M. F. ;

Srikant, K. ;

Sharma, A. K. ;

Tangri, S. K. ;

Suri, A. K. .

HYDROMETALLURGY, 2008, 91 (1-4) :28-34

← 1 2 →