Fatigue and fracture toughness of a Nb-Ti-Cr-Al-X single-phase alloy at ambient temperature

被引：20
|
作者：
Davidson, DL [1 ]
Chan, KS
Loloee, R
Crimp, MA
机构：
[1] SW Res Inst, San Antonio, TX 78238 USA
[2] Michigan State Univ, Dept Mat Sci & Mech, E Lansing, MI 48824 USA
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2000年 / 31卷 / 04期
关键词：
D O I：
10.1007/s11661-000-0103-5
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The fatigue and fracture resistance of a commercially made, single-phase Nb-base alloy with 35 at. pct Ti, 5 at. pct Cr, 6 at. pct Al, and several elements to increase solid solution strengthening have been investigated. The threshold for fatigue crack growth was determined to be approximate to 7 MPa root m and fracture toughness approximate to 35 MPa root m. Crack growth was intermittent and sporadic; the fracture path was tortuous, crystallographic, and appeared to favor the {100} and {112} planes. Fatigue crack closure was measured directly at the crack tip. The fatigue and fracture properties of the commercial alloy are compared against those of Nb-Cr-Ti and Nb-Cr-Ti-Al alloys. The comparison indicated that Ti addition is beneficial for, but Al addition is detrimental to, both fracture toughness and fatigue crack resistance.
引用
收藏
页码：1075 / 1084
页数：10
相关论文
共 50 条
  • [41] TENSILE　DEFORMATION　AND　FRACTURE　BEHAVIOR　OF　Ti3Al-Nb　ALLOY　AT　HIGH　TEMPERATURE
    Wu Ying
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA(ENGLISH EDITION), 1997, (01) : 76 - 82
  • [42] Tensile deformation and fracture behavior of Ti3Al-Nb alloy at high temperature
    Wu, Y
    Zhen, L
    Yang, DZ
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 1997, 7 (01) : 75 - 81
  • [43] Hydrogen absorption in as-cast bcc single-phase Ti-Al-Nb alloys
    Patselov, A. M.
    Rybin, V. V.
    Greenberg, B. A.
    Mushnikov, N. V.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 505 (01) : 183 - 187
  • [44] THE INFLUENCE OF CHEMICAL COMPOSITION ON THE PHASE BALANCE, MICROSTRUCTURE, HIGH-TEMPERATURE STRENGTH AND FRACTURE TOUGHNESS OF Ti-Si-X AND Ti-Cr-X COMPOSITES
    Kulyk, Volodymyr
    Vasyliv, Bogdan
    Duriagina, Zoia
    Lyutyy, Pavlo
    Vavrukh, Valentyna
    Kovbasiuk, Taras
    Vira, Volodymyr
    Holovchuk, Myroslav
    Loskutova, Tetiana
    ACTA METALLURGICA SLOVACA, 2022, 28 (01): : 33 - 42
  • [45] The effects on fracture toughness of ductile-phase composition and morphology in Nb-Cr-Ti and Nb-Si in situ composites
    Davidson, DL
    Chan, KS
    Anton, DL
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (10): : 3007 - 3018
  • [46] Effects on fracture toughness of ductile-phase composition and morphology in Nb-Cr-Ti and Nb-Si in situ composites
    Southwest Research Inst, San Antonio, United States
    Metall Mat Trans A Phys Metall Mat Sci, 10 (3007-3018):
  • [47] Room temperature mechanical strength and fracture behaviour of Nb-Ti-Si-Cr based alloy
    Su, L.
    Jia, L.
    Yuan, S.
    Zhou, L.
    Zhang, H.
    Zhang, H.
    MATERIALS SCIENCE AND TECHNOLOGY, 2015, 31 (02) : 220 - 224
  • [48] High temperature strength, fracture toughness and oxidation resistance of Nb-Si-Al-Ti multiphase alloys
    Murayama, Yonosuke
    Hanada, Shuji
    SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS, 2002, 3 (02) : 145 - 156
  • [49] Slip line formation during tensile straining experiments at ambient temperature in a Nb-Cr-Ti alloy
    Davidson, DL
    Chan, KS
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 282 (1-2): : 100 - 108
  • [50] Fracture toughness of Ti-15Al-8Nb alloy under mixed mode I/III loading
    Paradkar, A. G.
    Kamat, S. V.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (09): : 3283 - 3288
12345