Fatigue and fracture toughness of a Nb-Ti-Cr-Al-X single-phase alloy at ambient temperature

被引：20
|
作者：
Davidson, DL [1 ]
Chan, KS
Loloee, R
Crimp, MA
机构：
[1] SW Res Inst, San Antonio, TX 78238 USA
[2] Michigan State Univ, Dept Mat Sci & Mech, E Lansing, MI 48824 USA
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2000年 / 31卷 / 04期
关键词：
D O I：
10.1007/s11661-000-0103-5
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The fatigue and fracture resistance of a commercially made, single-phase Nb-base alloy with 35 at. pct Ti, 5 at. pct Cr, 6 at. pct Al, and several elements to increase solid solution strengthening have been investigated. The threshold for fatigue crack growth was determined to be approximate to 7 MPa root m and fracture toughness approximate to 35 MPa root m. Crack growth was intermittent and sporadic; the fracture path was tortuous, crystallographic, and appeared to favor the {100} and {112} planes. Fatigue crack closure was measured directly at the crack tip. The fatigue and fracture properties of the commercial alloy are compared against those of Nb-Cr-Ti and Nb-Cr-Ti-Al alloys. The comparison indicated that Ti addition is beneficial for, but Al addition is detrimental to, both fracture toughness and fatigue crack resistance.
引用
收藏
页码：1075 / 1084
页数：10
相关论文
共 50 条
  • [21] Effect of withdrawal rates on microstructures and room temperature fracture toughness in a directionally solidified Nb-Ti-Cr-Si based alloy
    Guo, Baohui
    Guo, Xiping
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 617 : 39 - 45
  • [22] Effect of notch root radius on fracture toughness of Ti-18Al-8Nb alloy
    Paradkar, A.
    Gogia, A. K.
    Kamat, S. V.
    MATERIALS SCIENCE AND TECHNOLOGY, 2009, 25 (04) : 515 - 519
  • [23] Microstructure characteristics of a γ single-phase Ti-55Al-7.5Nb alloy fabricated via additive manufacturing
    Xue, Hui
    Tong, Xinhuan
    Song, Yi
    Wang, Feng
    Liang, Yongfeng
    Peng, Hui
    Wang, Yanli
    Lin, Junpin
    INTERMETALLICS, 2023, 161
  • [24] Hot Deformation and Dynamic Recrystallization of Ti-6Al-7Nb Biomedical Alloy in Single-Phase β Region
    F. Pilehva
    A. Zarei-Hanzaki
    S. M. Fatemi-Varzaneh
    A. R. Khalesian
    Journal of Materials Engineering and Performance, 2015, 24 : 1799 - 1808
  • [25] Hot Deformation and Dynamic Recrystallization of Ti-6Al-7Nb Biomedical Alloy in Single-Phase β Region
    Pilehva, F.
    Zarei-Hanzaki, A.
    Fatemi-Varzaneh, S. M.
    Khalesian, A. R.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2015, 24 (05) : 1799 - 1808
  • [26] Microstructure Characterization and Fracture Toughness of Laves Phase-Based Cr-Nb-Ti Alloys
    Xue, Yun-Long
    Li, Shuang-Ming
    Zhong, Hong
    Li, Lai-Ping
    Fu, Heng-Zhi
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2015, 28 (04) : 514 - 520
  • [27] The interrelationship of fracture toughness and microstructure in a new near β titanium alloy Ti-7Mo-3Nb-3Cr-3Al
    Fan, J. K.
    Li, J. S.
    Kou, H. C.
    Hua, K.
    Tang, B.
    MATERIALS CHARACTERIZATION, 2014, 96 : 93 - 99
  • [28] High temperature strength and ambient temperature fracture toughness of Nb3Al/Nbss in-situ composites
    Hanada, S
    Tabaru, T
    Miura, E
    Gnanamoorthy, R
    Murayama, Y
    THERMEC '97 - INTERNATIONAL CONFERENCE ON THERMOMECHANICAL PROCESSING OF STEELS AND OTHER MATERIALS, VOLS I-II, 1997, : 1583 - 1588
  • [29] Phase stability in a Ti-45.5Al-2Nb-2Cr alloy
    Seetharaman, V
    Lombard, CM
    Semiatin, SL
    ADVANCES IN THE SCIENCE AND TECHNOLOGY OF TITANIUM ALLOY PROCESSING, 1996, : 497 - 506
  • [30] DEVELOPMENT OF A NEW HIGH FRACTURE TOUGHNESS TI ALLOY - TI-4.5AL-5MO-1.5CR
    FROES, FH
    BERRYMAN, RG
    WILLIAMS, JC
    CHESNUTT, JC
    RHODES, CG
    HIGHBERGER, WT
    JOM-JOURNAL OF METALS, 1975, 27 (12): : A39 - A39
12345