Corrosion Behaviour of Uncoated and Ceramic Coated 9Cr-1Mo Steel in Molten LiCl-KCl-UCl3 Salt

被引：3
|
作者：
Rao, Ch. Jagadeeswara [1 ]
Ismail, T. P. [2 ]
Shankar, A. Ravi [1 ]
Ballal, Atul Ramesh [2 ]
Mallika, C. [1 ]
Mudali, U. Kamachi [1 ]
机构：
[1] Indira Gandhi Ctr Atom Res, Corros Sci & Technol Grp, Kalpakkam 603102, Tamil Nadu, India
[2] Visvesvaraya Natl Inst Technol, Nagpur, Maharashtra, India
来源：
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2017年 / 70卷 / 05期
关键词：
Molten salt corrosion; 9Cr-1Mo steel; Plasma spray coating; Yttria stabilized zirconia; Corrosion behavior; HIGH-DENSITY GRAPHITE; STABILIZED ZIRCONIA COATINGS;
D O I：
10.1007/s12666-016-0906-8
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
9Cr-1Mo steel has been proposed as the container material for the electrorefining process of pyrochemical reprocessing of spent metallic fuels from the future sodium cooled fast breeder reactors. The electrorefining process was carried out using LiCl-KCl-UCl3 molten salt as the electrolyte at 500 A degrees C under argon atmosphere. To protect the electrorefining vessel, made of 9Cr-1Mo steel from the attack by the electrolyte, yttria stabilized zirconia (YSZ) ceramic coating was deposited on 9Cr-1Mo steel by thermal spray process. The corrosion behavior of 9Cr-1Mo steel with and without YSZ coating was evaluated in LiCl-KCl-UCl3 molten salt at 600 A degrees C under argon atmosphere for various durations (100, 250, 500 and 1000 h). The results revealed that with increase in exposure time, the weight loss of uncoated 9Cr-1Mo steel samples increased, while YSZ coated 9Cr-1Mo steel samples exhibited insignificant weight loss. SEM examination of exposed uncoated 9Cr-1Mo steel samples showed Cr depletion on the surface and formation of chromium based oxides as corrosion products. After the corrosion experiment, SEM/EDS and XRD analyses of both coated and uncoated samples showed the presence of Fe-Cr and UO2.
引用
收藏
页码：1359 / 1367
页数：9
相关论文
共 50 条
  • [41] Hot Corrosion Study of 9Cr–1Mo Boiler Steel Exposed to Different Molten Salt Mixtures
    Sumit Mahajan
    Rahul Chhibber
    Transactions of the Indian Institute of Metals, 2019, 72 : 2329 - 2348
  • [42] Metal dusting corrosion of 9Cr-1Mo steel in propane-butane gas mixture
    Grzesik, Z.
    Danielewski, M.
    Mrowecc, S.
    DIFFUSION IN MATERIALS - DIMAT2008, 2009, 289-292 : 477 - 483
  • [43] Dynamic fracture behaviour of thermo-mechanically processed modified 9Cr-1Mo steel
    Chatterjee, Arya
    Moitra, A.
    Bhaduri, A. K.
    Mitra, R.
    Chakrabarti, D.
    ENGINEERING FRACTURE MECHANICS, 2015, 149 : 74 - 88
  • [44] Characterization of Tempering Behaviour of Modified 9Cr-1Mo Steel by Ultrasonic Lamb wave Mixing
    Metya, Avijit Kr.
    Tarafder, Soumitra
    Balasubamaniam, Krishnaan
    MATERIALS TODAY-PROCEEDINGS, 2019, 11 : 695 - 699
  • [45] Effect of variation of external stress on the oxidation behaviour of 9Cr-1Mo steel at 973 K
    Pillai, SR
    Sivaibharasi, N
    Khatak, HS
    Gnanamoorthy, JB
    CORROSION AND ITS CONTROLS, VOLS I AND II, 1998, : 878 - 884
  • [46] Strain dependent constitutive analysis of hot deformation behaviour in 9Cr-1Mo ferritic steel
    Krishnan, S. A.
    Phaniraj, C.
    Ravishankar, C.
    Bhaduri, A. K.
    Sivaprasad, P. V.
    Raj, Baldev
    MATERIALS AT HIGH TEMPERATURES, 2012, 29 (01) : 33 - 40
  • [47] Effect of dynamic plastic deformation on microstructure and annealing behaviour of modified 9Cr-1Mo steel
    Zhang, Z. B.
    Mishin, O. V.
    Tao, N. R.
    Pantleon, W.
    MATERIALS SCIENCE AND TECHNOLOGY, 2015, 31 (06) : 715 - 721
  • [48] Zone-wise investigation of creep behaviour 9Cr-1Mo steel weld joints
    Yadav, Surya D.
    Vasantharaja, P.
    Riedlsperger, Florian
    Nagaraju, S.
    Vasudevan, M.
    MATERIALS SCIENCE AND TECHNOLOGY, 2019, 35 (02) : 155 - 172
  • [49] A comparison of high temperature corrosion behaviour between uncoated, Ni-Cr-Mo and Ni-Cr-Al-Y coated 316 stainless steel in ZnCl2-KCl environment
    Mangaladevi, Pooja
    Vijeesh, V.
    Ravishankar, K. S.
    Madav, Vasudeva
    RESULTS IN ENGINEERING, 2025, 25
  • [50] High-Temperature corrosion and cracking of 9Cr-1Mo steel coker Tube - A case study
    Poorhaydari, Kioumars
    ENGINEERING FAILURE ANALYSIS, 2025, 169
12345