Corrosion Behaviour of Uncoated and Ceramic Coated 9Cr-1Mo Steel in Molten LiCl-KCl-UCl3 Salt

被引：3

作者：

Rao, Ch. Jagadeeswara ^{[1
]}

Ismail, T. P. ^{[2
]}

Shankar, A. Ravi ^{[1
]}

Ballal, Atul Ramesh ^{[2
]}

Mallika, C. ^{[1
]}

Mudali, U. Kamachi ^{[1
]}

机构：

[1] Indira Gandhi Ctr Atom Res, Corros Sci & Technol Grp, Kalpakkam 603102, Tamil Nadu, India

[2] Visvesvaraya Natl Inst Technol, Nagpur, Maharashtra, India

来源：

TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2017年 / 70卷 / 05期

关键词：

Molten salt corrosion; 9Cr-1Mo steel; Plasma spray coating; Yttria stabilized zirconia; Corrosion behavior; HIGH-DENSITY GRAPHITE; STABILIZED ZIRCONIA COATINGS;

D O I：

10.1007/s12666-016-0906-8

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

9Cr-1Mo steel has been proposed as the container material for the electrorefining process of pyrochemical reprocessing of spent metallic fuels from the future sodium cooled fast breeder reactors. The electrorefining process was carried out using LiCl-KCl-UCl3 molten salt as the electrolyte at 500 A degrees C under argon atmosphere. To protect the electrorefining vessel, made of 9Cr-1Mo steel from the attack by the electrolyte, yttria stabilized zirconia (YSZ) ceramic coating was deposited on 9Cr-1Mo steel by thermal spray process. The corrosion behavior of 9Cr-1Mo steel with and without YSZ coating was evaluated in LiCl-KCl-UCl3 molten salt at 600 A degrees C under argon atmosphere for various durations (100, 250, 500 and 1000 h). The results revealed that with increase in exposure time, the weight loss of uncoated 9Cr-1Mo steel samples increased, while YSZ coated 9Cr-1Mo steel samples exhibited insignificant weight loss. SEM examination of exposed uncoated 9Cr-1Mo steel samples showed Cr depletion on the surface and formation of chromium based oxides as corrosion products. After the corrosion experiment, SEM/EDS and XRD analyses of both coated and uncoated samples showed the presence of Fe-Cr and UO2.

引用

页码：1359 / 1367

页数：9

共 50 条

[21] Flow Behaviour of Modified 9Cr-1Mo Steel at Elevated Temperatures
Shiva, V.
Goyal, Sunil
Sandhya, R.
Laha, K.
Bhaduri, A. K.
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2017, 70 (03) : 589 - 596
[22] Corrosion behaviour of nano structured sol-gel alumina coated 9Cr-1Mo ferritic steel in chloride bearing environments
Ruhi, G.
Modi, O. P.
Singh, I. B.
SURFACE & COATINGS TECHNOLOGY, 2009, 204 (03): : 359 - 365
[23] High-temperature electrochemical corrosion evaluation of 2.25Cr-1Mo alloy in eutectic LiCl-KCl molten salt
Rao, Ch Jagadeeswara
Ningshen, S.
CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2022, 57 (01) : 66 - 73
[24] ELEVATED TEMPERATURE EROSION-CORROSION OF 9Cr-1Mo STEEL.
Levy, Alan
Man, Yong-Fa
1600, (111):
[25] Microstructural and corrosion studies of 9Cr-1Mo steel in acidic methanol solutions
Singh, VB
Gupta, A
INDIAN JOURNAL OF CHEMICAL TECHNOLOGY, 2005, 12 (03) : 347 - 355
[26] Unified tensile work hardening behaviour of 9Cr-1Mo ferritic steel
Choudhary, B. K.
Palaparti, D. P. Rao
Samuel, E. Isaac
Jayakumar, T.
MATERIALS SCIENCE AND TECHNOLOGY, 2013, 29 (03) : 278 - 284
[27] Creep deformation behaviour and kinetic aspects of 9Cr-1Mo ferritic steel
Choudhary, BK
Phaniraj, C
Rao, KBS
Mannan, SL
ISIJ INTERNATIONAL, 2001, 41 : S73 - S80
[28] Creep Deformation Behaviour of Modified 9Cr-1Mo Steel Clad Tubes
Latha, S.
Laha, K.
Parameswaran, P.
Reddy, G. V. Prasad
Sasikala, G.
Albert, Shaju K.
STRUCTURAL INTEGRITY ASSESSMENT, ICONS 2018, 2020, : 387 - 396
[29] Influence of Anions on the Corrosion Behavior of 9Cr-1Mo Ferritic Steel in Aqueous Media
Thinaharan, C.
Vanithakumari, S. C.
Shankar, A. Ravi
Philip, John
CORROSION, 2023, 79 (10) : 1192 - 1209
[30] Influence of normalizing heat treatment on precipitation behaviour in modified 9Cr-1Mo steel
Yoshino, Masataka
Mishima, Yoshinao
Toda, Yoshiaki
Kushima, Hideaki
Sawada, Kota
Kimura, Kazuhiro
MATERIALS AT HIGH TEMPERATURES, 2008, 25 (03) : 149 - 158

← 1 2 3 4 5 →