Tensile fatigue behavior of tapered glass fiber reinforced epoxy composites containing nanoclay

被引：31
|
作者：
Helmy, S. [1 ]
Hoa, S. V. [1 ]
机构：
[1] Concordia Univ, Ctr Res Polymers & Composites CREPEC, Dept Mech & Ind Engn, Montreal, PQ H3G 1M8, Canada
来源：
COMPOSITES SCIENCE AND TECHNOLOGY | 2014年 / 102卷
关键词：
Glass fibers; Nanoclays; Polymer matrix composites (PMCs); Fatigue; Matrix cracking; INTERLAMINAR STRESSES; MECHANICAL-PROPERTIES; LIFE METHODOLOGY; NANOCOMPOSITES; DELAMINATION; FRACTURE; PERFORMANCE; STRENGTH; MATRIX; CFRP;
D O I：
10.1016/j.compscitech.2014.05.038
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
Tensile fatigue behavior of tapered glass/epoxy laminates is investigated. The effect of nanoclay addition into the epoxy resin is examined. It is shown that the relative orientation between the adjacent belt layer and the cut layer has important influence on the fatigue life. The fatigue crack starts at the resin pocket and propagates along the interface between the belt layer and the core layer in the thicker section of the laminate. Crack propagation is mainly due to mode II crack failure. The addition of the clays enhances the resistance against this mode II crack propagation, and thus prolongs the fatigue life of the laminate. (C) 2014 Elsevier Ltd. All rights reserved.
引用
收藏
页码：10 / 19
页数：10
相关论文
共 50 条
  • [21] Mechanical Behavior of Hybrid Glass/Steel Fiber Reinforced Epoxy Composites
    McBride, Amanda K.
    Turek, Samuel L.
    Zaghi, Arash E.
    Burke, Kelly A.
    POLYMERS, 2017, 9 (04):
  • [22] Tensile properties of plain weft knitted glass fiber fabric reinforced epoxy composites
    J Reinf Plast Compos, 10 (946-966):
  • [23] The noteworthy tensile plasticity and strength of CoFeSiB metallic glass fiber reinforced epoxy composites
    Liang, Weizhong
    Shao, Qi
    Liu, Yingyi
    Wei, Ransong
    Xu, Jiawen
    POLYMER COMPOSITES, 2024, 45 (15) : 14257 - 14267
  • [24] Tensile properties of plain weft knitted glass fiber fabric reinforced epoxy composites
    Ramakrishna, S
    Cuong, NK
    Hamada, H
    JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1997, 16 (10) : 946 - 966
  • [25] GLASS FIBER-REINFORCED EPOXY COMPOSITES
    PATEL, SR
    PATEL, RG
    ANGEWANDTE MAKROMOLEKULARE CHEMIE, 1992, 197 : 141 - 147
  • [26] Experimental Investigation on the Fatigue Behavior of Glass Fiber-Reinforced Epoxy Composites Under Rotating Bending Loads
    Hemanth Kumar, C.
    Swamy, R. P.
    JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2021, 21 (02) : 582 - 587
  • [27] Experimental Investigation on the Fatigue Behavior of Glass Fiber-Reinforced Epoxy Composites Under Rotating Bending Loads
    C. Hemanth Kumar
    R. P. Swamy
    Journal of Failure Analysis and Prevention, 2021, 21 : 582 - 587
  • [28] The Tensile Fatigue Behavior of a Glass-fiber Reinforced Plastic Composite Using a Hybrid-toughened Epoxy Matrix
    Manjunatha, C. M.
    Sprenger, S.
    Taylor, A. C.
    Kinloch, A. J.
    JOURNAL OF COMPOSITE MATERIALS, 2010, 44 (17) : 2095 - 2109
  • [29] Impact resistance of hybrid glass fiber reinforced epoxy/nanoclay composite
    Rafiq, Ahmad
    Merah, Nesar
    Boukhili, Rachid
    Al-Qadhi, Muneer
    POLYMER TESTING, 2017, 57 : 1 - 11
  • [30] Static and fatigue behavior of basalt fiber-reinforced thermoplastic epoxy composites
    Wang, Xin
    Zhao, Xing
    Chen, Siqi
    Wu, Zhishen
    JOURNAL OF COMPOSITE MATERIALS, 2020, 54 (18) : 2389 - 2398
12345