Crack healing in polymeric materials via photochemical [2+2] cycloaddition

被引:370
作者
Chung, CM [1 ]
Roh, YS
Cho, SY
Kim, JG
机构
[1] Yonsei Univ, Dept Chem, Kangwon Do 220710, South Korea
[2] Hanwha Chem R&D Ctr, Div Biotechnol, Taejon 305345, South Korea
关键词
D O I
10.1021/cm049394+
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Photochemical crack healing in a polymeric material was accomplished by employing a tricinnamate monomer. A cross-linked network was obtained via [2 + 2] photocycloaddition of the monomer, and the resulting cyclobutane cross-links reversed to the original cinnamoyl groups upon crack formation. Crack healing was achieved via re-photocycloaddition of cinnamoyl groups.
引用
收藏
页码:3982 / +
页数:4
相关论文
共 22 条
[1]  
Ali AH, 1997, POLYM INT, V43, P310
[2]  
ARAU N, 1993, PHOTOCHEMISTRY POLYM, P15
[3]   A thermally re-mendable cross-linked polymeric material [J].
Chen, XX ;
Dam, MA ;
Ono, K ;
Mal, A ;
Shen, HB ;
Nutt, SR ;
Sheran, K ;
Wudl, F .
SCIENCE, 2002, 295 (5560) :1698-1702
[4]   KALEIDOSCOPIC PHOTOREACTION BEHAVIOR OF ALKYL 4-[2-(4-PYRIDYL)ETHENYL]CINNAMATE CRYSTALS - A CRYSTALLINE LINEAR HIGH POLYMER FROM THE METHYL-ESTER, AN ABSOLUTE ASYMMETRIC REACTION OF THE ETHYL-ESTER, AND 2 TYPES OF DIMER FORMATION FROM THE PROPYL ESTER [J].
CHUNG, CM ;
HASEGAWA, M .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1991, 113 (19) :7311-7316
[5]  
CRAIG RG, 2002, RESTORATIVE DENTAL M, P191
[7]  
DECKER C, 1993, ROY SOC CH, V125, P32
[8]   Procedures developed for self-repair of polymer matrix composite materials [J].
Dry, C .
COMPOSITE STRUCTURES, 1996, 35 (03) :263-269
[9]  
EGERTON PL, 1981, J AM CHEM SOC, V103, P3859, DOI 10.1021/ja00403a039
[10]   Photolytic and free-radical polymerization of cinnamate esters of epoxidized plant oil triglycerides [J].
Esen, H ;
Küsefoglu, SH .
JOURNAL OF APPLIED POLYMER SCIENCE, 2003, 89 (14) :3882-3888