Composition, structure and mechanical properties of metal oxide coatings produced on titanium using plasma spraying and modified by micro-arc oxidation

被引：35

作者：

Koshuro, Vladimir ^{[1
]}

Fomin, Aleksandr ^{[1
]}

Rodionov, Igor ^{[1
]}

机构：

[1] Yuri Gagarin State Tech Univ Saratov, Inst Elect Technol & Engn, 77 Politech Skaya Str, Saratov 410054, Russia

来源：

CERAMICS INTERNATIONAL | 2018年 / 44卷 / 11期

关键词：

Alumina; Plasma spraying; Titania; Micro-arc oxidation; BIOMEDICAL APPLICATIONS; ELECTROLYTIC OXIDATION; CORROSION-RESISTANCE; THERMAL-OXIDATION; SURFACE-TREATMENT; DENTAL IMPLANTS; ALLOYS; MICROSTRUCTURE; INDUCTION;

D O I：

10.1016/j.ceramint.2018.04.056

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Metal oxide coatings on VT6 titanium alloy were formed by plasma spraying of aluminum oxide powder and subsequent microarc oxidation at a current density from 1 to 3 kA/m(2). As a result of combined treatment, metal oxide coatings consisting of a mixture of aluminum and titanium oxides were obtained on the surface of titanium samples. The most pronounced changes in the morphology of the plasma-sprayed coating were observed at the highest current density of 3 kA/m(2). The open porosity decreased from 56% to 38% due to the modification by micro-arc discharges, whereas the microhardness increased from 1013 +/- 150 HV to 1639 +/- 31 HV.

引用

页码：12593 / 12599

页数：7

共 40 条

[21] Surface treatments of titanium dental implants for rapid osseointegration [J].

Le Guehennec, L. ;

Soueidan, A. ;

Layrolle, P. ;

Amouriq, Y. .

DENTAL MATERIALS, 2007, 23 (07) :844-854

[22] Plasma surface treatment of aerospace materials for enhanced adhesive bonding [J].

Leahy, W ;

Barron, V ;

Buggy, M ;

Young, T ;

Mas, A ;

Schue, F ;

McCabe, T ;

Bridge, M .

JOURNAL OF ADHESION, 2001, 77 (03) :215-249

[23] Thermal oxidation of Ti6Al4V alloy and its biotribological properties under serum lubrication [J].

Luo, Yong ;

Chen, Wenwen ;

Tian, Maocai ;

Teng, Shuhua .

TRIBOLOGY INTERNATIONAL, 2015, 89 :67-71

[24] MACHINING OF TITANIUM AND ITS ALLOYS - A REVIEW [J].

MACHADO, AR ;

WALLBANK, J .

PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART B-JOURNAL OF ENGINEERING MANUFACTURE, 1990, 204 (01) :53-60

[25] Investigation of surface pre-treatments for the structural bonding of titanium [J].

Mertens, T. ;

Gammel, F. J. ;

Kolb, M. ;

Rohr, O. ;

Kotte, L. ;

Tschoecke, S. ;

Kaskel, S. ;

Krupp, U. .

INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2012, 34 :46-54

[26] Mechanical biocompatibilities of titanium alloys for biomedical applications [J].

Niinomi, Mitsuo .

JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS, 2008, 1 (01) :30-42

[27] Effect of heat-treatment on stress relaxation behavior of plasma-sprayed 7 wt.% Y2O3-ZrO2 stand-alone coatings [J].

Petorak, Christopher ;

Trice, Rodney W. .

SURFACE & COATINGS TECHNOLOGY, 2011, 205 (10) :3218-3225

[28] Gas turbine coatings - An overview [J].

Rajendran, R. .

ENGINEERING FAILURE ANALYSIS, 2012, 26 :355-369

[29] Pulsed ion beam-assisted carburizing of titanium in methane discharge [J].

Shafiq, M. ;

Hassan, M. ;

Shahzad, K. ;

Qayyum, A. ;

Ahmad, S. ;

Rawat, R. S. ;

Zakaullah, M. .

CHINESE PHYSICS B, 2010, 19 (01)

[30] Thermal oxidation of titanium to improve corrosion resistance in boiling nitric acid medium [J].

Shankar, A. Ravi ;

Karthiselva, N. S. ;

Mudali, U. Kamachi .

SURFACE & COATINGS TECHNOLOGY, 2013, 235 :45-53

← 1 2 3 4 →