Enhancement in thermoelectric performance of electrochemically deposited platinum-bismuth telluride nanocomposite

被引：29

作者：

Samat, Khairul Fadzli ^{[1
,2
]}

Nguyen Huu Trung ^{[1
]}

Ono, Takahito ^{[1
]}

机构：

[1] Tohoku Univ, Grad Sch Engn, Aoba Ku, Sendai, Miyagi 9808579, Japan

[2] Univ Teknikal Malaysia Melaka, Fak Kejuruteraan Pembuatan, Durian Tunggal 76100, Melaka, Malaysia

来源：

ELECTROCHIMICA ACTA | 2019年 / 312卷

关键词：

Bismuth telluride; Platinum nanoparticles; Nanocomposite; Electrodeposition; Nano-inclusion; THERMAL-CONDUCTIVITY; BI2TE3; FILMS; THIN-FILMS; NANOPARTICLES; ELECTRODEPOSITION; MICROSTRUCTURE; FIGURE; PH;

D O I：

10.1016/j.electacta.2019.04.139

中图分类号：

O646 [电化学、电解、磁化学];

学科分类号：

081704 ;

摘要：

The study of the thermoelectric performance of electrodeposited Pt nanoparticles-bismuth telluride nanocomposites (Pt/Bi2Te3) film is presented in this paper. An electrolyte solution containing nitric acid and bismuth-telluride ions was mixed with various concentrations of Pt nanoparticles.1.0 wt% to 1.9 wt% of Pt nanoparticles in the composites have been successfully synthesized and their thermoelectric performances were investigated. It is found that at 1.9% of Pt nanoparticles weight percentage in the Bi2Te3 matrix, the power factor increased to 1.8 x 10(-3) W m(-1) K-2 which is more than twice higher than that of an electrodeposited pure Bi2Te3 film. Meanwhile, the evaluation on thermal conductivity of the composite shows promising improvement, which is more than 40% reduction as compared to the Bi2Te3 film. As a result, a higher ZT value of 0.61 is obtained for the Pt (1.9 wt%)/Bi2Te3 film which is approximately more than triple of ZT of the electrodeposited Bi2Te3 film at room temperature. (C) 2019 Elsevier Ltd. All rights reserved.

引用

页码：62 / 71

页数：10

共 56 条

[1]

[Anonymous], 2002, F76 ASTM INT, P86

[2]

[Anonymous], [No title captured]

[3]

[Anonymous], 2008, HALL EFFECT MEASUREM

[4] Thermal conduction in doped single-crystal silicon films [J].

Asheghi, M ;

Kurabayashi, K ;

Kasnavi, R ;

Goodson, KE .

JOURNAL OF APPLIED PHYSICS, 2002, 91 (08) :5079-5088

[5] Influence of bath composition and pH on the electrocodeposition of alumina nanoparticles and nickel [J].

Bund, Andreas ;

Thiemig, Denny .

SURFACE & COATINGS TECHNOLOGY, 2007, 201 (16-17) :7092-7099

[6] Approximation of crystallite size and microstrain via XRD line broadening analysis in TiSiN thin films [J].

Bushroa, A. R. ;

Rahbari, R. G. ;

Masjuki, H. H. ;

Muhamad, M. R. .

VACUUM, 2012, 86 (08) :1107-1112

[7] THERMAL-CONDUCTIVITY OF ALPHA-SIH THIN-FILMS [J].

CAHILL, DG ;

KATIYAR, M ;

ABELSON, JR .

PHYSICAL REVIEW B, 1994, 50 (09) :6077-6081

[8] Thermometry and thermal transport in micro/nanoscale solid-state devices and structures [J].

Cahill, DG ;

Goodson, KE ;

Majumdar, A .

JOURNAL OF HEAT TRANSFER-TRANSACTIONS OF THE ASME, 2002, 124 (02) :223-241

[9] THERMAL-CONDUCTIVITY MEASUREMENT FROM 30-K TO 750-K - THE 3-OMEGA METHOD [J].

CAHILL, DG .

REVIEW OF SCIENTIFIC INSTRUMENTS, 1990, 61 (02) :802-808

[10] Ultralow Lattice Thermal Conductivity of the Random Multilayer Structure with Lattice Imperfections [J].

Chakraborty, Pranay ;

Cao, Lei ;

Wang, Yan .

SCIENTIFIC REPORTS, 2017, 7

← 1 2 3 4 5 6 →