Microstructural changes and corrosion resistance of AISI 310S steel exposed to 600-800°C

被引：58
作者：
Tavares, S. S. M. [1 ]
Moura, V. [1 ]
da Costa, V. C. [1 ]
Ferreira, M. L. R. [1 ]
Pardal, J. M. [1 ]
机构：
[1] Univ Fed Fluminense, Dept Engn Mecan, BR-24210240 Niteroi, RJ, Brazil
来源：
MATERIALS CHARACTERIZATION | 2009年 / 60卷 / 06期
关键词：
Austenitic stainless steel; AISI; 310; Sensitization; Sigma phase precipitation; SIGMA-PHASE; MECHANICAL-PROPERTIES; STAINLESS-STEELS; TEMPERATURE;
D O I：
10.1016/j.matchar.2008.12.005
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The microstructural changes in an AISI 310S stainless steel exposed to temperatures in the 600-800 degrees C range up to 210 h were investigated. intense carbide precipitation occurs in all conditions. Sigma phase precipitation nucleates at the grain boundaries and becomes more intense with the increase of time and temperature. Intergranular corrosion resistance was evaluated by double loop electrochemical potentiodynamic reactivation tests. Sigma phase and chromium carbides cause severe sensitization, but healing is observed in specimens aged at 650 degrees C, 700 degrees C, 750 degrees C and 800 degrees C. Time to healing decreases with the increase of aging temperature. Anodic polarization tests were conducted in specimens aged for 210 h. Pitting potentials are found to decrease in all temperature tested. (C) 2008 Elsevier Inc. All rights reserved.
引用
收藏
页码：573 / 578
页数：6
相关论文
共 15 条
  • [1] [Anonymous], 2003, DUPLEX STAINLESS STE
  • [2] *ASTM, 1998, A24097A ASTM
  • [3] Cracking of the mixing chamber caused by sigma phase precipitation in austenitic steel welded joints
    Brozda, J.
    Madej, J.
    [J]. ENGINEERING FAILURE ANALYSIS, 2008, 15 (04) : 368 - 377
  • [4] FARRAR JCM, 1999, STAINL STEEL WORLD 9, P147
  • [5] The role of temperature on the corrosion and passivation of type 310S stainless steel in eutectic (Li+K) carbonate melt
    Frangini, S.
    Loreti, S.
    [J]. JOURNAL OF POWER SOURCES, 2006, 160 (02) : 800 - 804
  • [6] Microstructure and intergranular corrosion resistance evaluation of AISI 304 steel for high temperature service
    Kina, A. Yae
    Souza, V. M.
    Tavares, S. S. M.
    Pardal, J. M.
    Souza, J. A.
    [J]. MATERIALS CHARACTERIZATION, 2008, 59 (05) : 651 - 655
  • [7] Influence of σ-phase on mechanical properties and corrosion resistance of duplex stainless steels
    Lopez, N
    Cid, M
    Puiggali, M
    [J]. CORROSION SCIENCE, 1999, 41 (08) : 1615 - 1631
  • [8] Application of double loop electrochemical potentiodynamic reactivation test to austenitic and duplex stainless steels
    Lopez, N
    Cid, M
    Puiggali, M
    Azkarate, I
    Pelayo, A
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 229 (1-2): : 123 - 128
  • [9] MAYO EW, 1997, MAT SCI ENG A-STRUCT, V252, P129
  • [10] Mechanical properties, microstructural stability and kinetics of σ-phase formation in 29Cr-6Ni-2Mo-0.38N superduplex stainless steel
    Nilsson, JO
    Kangas, P
    Karlsson, T
    Wilson, A
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (01): : 35 - 45
12