Kinetics of solid-state reactions between zirconium thin film and silicon carbide at elevated temperatures

Solid state reactions between a thin film (133 nm) of Zr and bulk single crystalline 6H-SiC substrates have been studied at temperatures between 600 degrees C and 850 degrees C for durations of 30, 60 and 120 min under high vacuum conditions. The deposited film and reaction zones were investigated by Rutherford backscattering spectrometry (RBS) and X-ray diffraction. The RBS spectra were simulated in order to obtain the deposited layer thickness, reaction zone compositions and reaction zone thickness. The as-deposited spectra fit well with those annealed at 600 degrees C, thus showing there were no reactions taking place. At temperatures of 700 degrees C and above, Zr reacted with the SiC substrate and formed a mixed layer of Zr carbide (ZrCx) and Zr silicides (ZrSi, Zr2Si and Zr5Si3). Annealing at 850 degrees C for 240 min revealed that all the deposited Zr had completely reacted. The interface reaction follows the parabolic growth law thereby indicating diffusion controlled reaction kinetics. The activation energy for the diffusion process obtained was 1.6 eV in the relatively narrow temperature range 700-850 degrees C. (C) 2014 Elsevier B.V. All rights reserved.