Fabrication of tailored alumina-based ceramics through colloidal processing

被引:4
作者
Sakka, Y [1 ]
Suzuki, TS [1 ]
Hiraga, K [1 ]
机构
[1] Natl Inst Mat Sci, Tsukuba, Ibaraki 3050047, Japan
来源
HIGH-PERFORMANCE CERAMICS 2001, PROCEEDINGS | 2002年 / 224-2卷
关键词
colloidal processing; Al2O3; super-plasticity; high magnetic field; textured structure;
D O I
10.4028/www.scientific.net/KEM.224-226.619
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Super-plastic zirconia-dispersed alumina ceramics with fine-grained microstructure and the other is highly textured alumina were prepared. Colloidal processing was applied to obtain dense and homogeneous zirconia-dispersed alumina ceramics with mean grain size of 0.45 mum. Large tensile elongation exceeding 550% was achieved for 10 vol% zirconia-dispersed Al2O3 at 1773K, High magnetic field (10T) was applied during slip casting of alumina suspension to produce textured microstructure. Green body with slight degree of crystallographic orientation was obtained and the degree of texture increased with increasing temperature. After densification, alumina grains grow to yield cerarnics with textured grains and high degrees of crystallographic orientation. This processing can be applied to other ceramics with asymmetric unit cell.
引用
收藏
页码:619 / 622
页数:4
相关论文
共 13 条
  • [1] LEVITATION OF ORGANIC MATERIALS
    BEAUGNON, E
    TOURNIER, R
    [J]. NATURE, 1991, 349 (6309) : 470 - 470
  • [2] Cavitation damage mechanisms in a superplastic zirconia(3Y-TZP)
    Hiraga, K
    Nakano, K
    [J]. SUPERPLASTICITY IN ADVANCED MATERIALS - ICSAM-97, 1997, 243-2 : 387 - 392
  • [3] Cavitation damage during high temperature tensile deformation in fine-grained alumina doped with magnesia or zirconia
    Hiraga, K
    Nakano, K
    Suzuki, TS
    Sakka, Y
    [J]. SCRIPTA MATERIALIA, 1998, 39 (09) : 1273 - 1279
  • [4] HIRAGA K, 1999, ICM8, V3, P981
  • [5] Superplastic tensile ductility enhanced by grain size refinement in a zirconia-dispersed alumina
    Nakano, K
    Suzuki, TS
    Hiraga, K
    Sakka, Y
    [J]. SCRIPTA MATERIALIA, 1997, 38 (01) : 33 - 38
  • [6] Preparation methods and superplastic properties of fine-grained zirconia and alumina based ceramics
    Sakka, Y
    Hiraga, K
    [J]. NIPPON KAGAKU KAISHI, 1999, (08) : 497 - 508
  • [7] Colloidal processing and superplastic properties of zirconia- and alumina-based nanocomposites
    Sakka, Y
    Suzuki, TS
    Morita, K
    Nakano, K
    Hiraga, K
    [J]. SCRIPTA MATERIALIA, 2001, 44 (8-9) : 2075 - 2078
  • [8] Fabrication of textured alumina through slip casting in a high magnetic field and heating
    Sakka, Y
    Suzuki, TS
    Kitazawa, K
    [J]. EURO CERAMICS VII, PT 1-3, 2002, 206-2 : 349 - 352
  • [9] Controls of precipitating phase alignment and crystal orientation using high magnetic field
    Sassa, K
    Morikawa, H
    Asai, S
    [J]. JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1997, 61 (12) : 1283 - 1287
  • [10] Suzuki TS, 2001, J AM CERAM SOC, V84, P2132, DOI 10.1111/j.1151-2916.2001.tb00973.x