Characterization of porous silicon nitride ceramics by pressureless sintering using fly ash cenosphere as a pore-forming agent

被引：56
|
作者：
Shao, Yingfeng [1 ]
Jia, Dechang [1 ]
Liu, Boyang [1 ]
机构：
[1] Harbin Inst Technol, Inst Adv Ceram, Harbin 150001, Peoples R China
来源：
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2009年 / 29卷 / 08期
基金：
中国国家自然科学基金;
关键词：
Sintering; Porosity; Mechanical properties; Si3N4; FABRICATION; STRENGTH; POROSITY;
D O I：
10.1016/j.jeurceramsoc.2008.09.012
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
A new method for fabricating porous silicon nitride ceramics has been developed by using fly ash cenosphere (FAC) with mean diameter of 87 mu m as a pore-forming agent. Sintering was carried out at 1780 degrees C for 2 It under a nitrogen atmosphere. FAC can also act as a sintering aid besides a pore-forming agent. X-ray diffraction (XRD) and transmission electron microscopy (TEM) studies showed that YSiO2N forms instead of Y2Si3O3N4 when FAC is incorporated. Microstructural analysis revealed that large spherical cavities are scattered in a relative dense matrix. Porous Si3N4 ceramics with density of 2.17-2.30g/cm(3), Young's modulus of 141-150 GPa and strength of 180-320 MPa were obtained by changing the FAC content. (c) 2008 Elsevier Ltd. All rights reserved.
引用
收藏
页码：1529 / 1534
页数：6
相关论文
共 50 条
  • [1] Preparation of Porous Mullite Ceramics Using Fly Ash Cenosphere as a Pore-Forming Agent by Gelcasting Process
    Qian, Haoran
    Cheng, Xudong
    Zhang, Heping
    Zhang, Ruifang
    Wang, Yonghong
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2014, 11 (05) : 858 - 863
  • [2] Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent
    Yang, Yulong
    Liu, Fengli
    Chang, Qibing
    Hu, Zhiwen
    Wang, Qikun
    Wang, Yongqing
    CERAMICS-SWITZERLAND, 2019, 2 (02): : 286 - 295
  • [3] Preparation of porous β-SiAlON ceramics using corn starch as pore-forming agent
    Liu, Xin
    Yu, Chen
    Qu, Dianli
    Luo, Xudong
    JOURNAL OF THE AUSTRALIAN CERAMIC SOCIETY, 2022, 58 (02) : 531 - 537
  • [4] Preparation and properties of porous silicon nitride ceramics with uniform spherical pores by improved pore-forming agent method
    Zhou, Jun
    Fan, Jin-peng
    Sun, Ge-liang
    Zhang, Jing-yi
    Liu, Xiao-ming
    Zhang, Da-hai
    Wang, Hong-jie
    JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 632 : 655 - 660
  • [5] Porous ceramics prepared using poppy seed as a pore-forming agent
    Gregorova, Eva
    Pabst, Willi
    CERAMICS INTERNATIONAL, 2007, 33 (07) : 1385 - 1388
  • [6] The preparation and characterization of porous alumina ceramics using an eco-friendly pore-forming agent
    Alzukaimi, Julian
    Jabrah, Rafi
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2019, 16 (02) : 820 - 831
  • [7] Pressureless Sintering of Silicon Nitride Porous Ceramics with High Porosity and Bimodal Pore Structure
    Chen, Fei
    Shen, Qiang
    Zhang, Lianmeng
    HIGH-PERFORMANCE CERAMICS VII, PTS 1 AND 2, 2012, 512-515 : 873 - +
  • [8] Elastic properties of porous oxide ceramics prepared using starch as a pore-forming agent
    Zivcova, Zuzana
    Cerny, Martin
    Pabst, Willi
    Gregorova, Eva
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2009, 29 (13) : 2765 - 2771
  • [9] CORN STARCH AS A PORE-FORMING AGENT AND MICROSTRUCTURAL CHARACTERIZATION OF POROUS CERAMICS BY IMAGE ANALYSIS
    Gregorova, Eva
    Chmelickova, Michaela
    Pabst, Willi
    PROCEEDINGS OF THE 6TH INTERNATIONAL CONFERENCE ON POLYSACCHARIDES-GLYCOSCIENCE, 2010, : 91 - 95
  • [10] Tailored pore structures and mechanical properties of porous alumina ceramics prepared with corn cob pore-forming agent
    Dele-Afolabi, T. T.
    Hanim, M. A. Azmah
    Ojo-Kupoluyi, O. J.
    Calin, R.
    Zuhri, M. Y. M.
    INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY, 2021, 18 (01) : 244 - 252
12345