Implication of grain boundary engineering on high temperature hot corrosion of alloy 617

被引：75
作者：
Deepak, K. [1 ]
Mandal, Sumantra [2 ]
Athreya, C. N. [1 ]
Kim, Dong-Ik [3 ]
de Boer, B. [4 ]
Sarma, V. Subramanya [1 ]
机构：
[1] Indian Inst Technol, Dept Met & Mat Engn, Madras 600036, Tamil Nadu, India
[2] Indian Inst Technol, Dept Met & Mat Engn, Kharagpur 721302, W Bengal, India
[3] Korea Inst Sci & Technol, High Temp Energy Mat Res Ctr, Seoul 02792, South Korea
[4] VDM Met GmbH, Plettenberger Str 2, D-58791 Werdohl, Germany
来源：
CORROSION SCIENCE | 2016年 / 106卷
关键词：
Superalloys; SEM; High temperature corrosion; Segregation; SUPERALLOY; BEHAVIOR; SENSITIZATION; RESISTANT; STRAIN; WATER;
D O I：
10.1016/j.corsci.2016.01.019
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The role of grain boundary engineering (GBE) on high-temperature hot corrosion behavior of alloy 617 was evaluated by exposing both the as-received (AR) and GBE specimens in a salt-mixture of (75% Na2SO4 + 20% NaCl + 5% V2O5) at 1273 K for 24 h. The AR specimen having continuous network of random high angle grain boundaries (HAGBs) has undergone hot corrosion and substantial depletion/segregation of alloying elements through the entire cross section. The GBE specimen exhibited significantly reduced hot corrosion and depletion/segregation of alloying elements. This is attributed to the high fraction of 3-CSL triple junctions which break the percolation in the random HAGBs network. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：293 / 297
页数：5
相关论文
共 50 条
[31]   Solving oxygen embrittlement of refractory high-entropy alloy via grain boundary engineering [J].
Wang, Zhengqi ;
Wu, Honghui ;
Wu, Yuan ;
Huang, Hailong ;
Zhu, Xiangyu ;
Zhang, Yingjie ;
Zhu, Huihui ;
Yuan, Xiaoyuan ;
Chen, Qiang ;
Wang, Shudao ;
Liu, Xiongjun ;
Wang, Hui ;
Jiang, Suihe ;
Kim, Moon J. ;
Lu, Zhaoping .
MATERIALS TODAY, 2022, 54 :83-89
[32]   Mechanism of grain boundary serration during hot deformation of AZ31 alloy: Role of grain boundary dislocations and grain boundary sliding [J].
Son, Hyeon-Woo ;
Lee, Ji-Woon ;
Hyun, Soong-Keun .
INTERNATIONAL JOURNAL OF PLASTICITY, 2020, 125 :118-132
[33]   High temperature electrochemical sensor for in situ monitoring of hot corrosion [J].
Aung, Naing Naing ;
Liu, Xingbo .
CORROSION SCIENCE, 2012, 65 :1-4
[34]   Comparison of high temperature hot corrosion behavior of AlCoCrFeNiTi and AlCoCrFeNiZr high entropy alloy (HEAs) coatings [J].
Odabas, Okan ;
Ozgurluk, Yasin ;
Karaoglanli, Abdullah Cahit .
SURFACE & COATINGS TECHNOLOGY, 2025, 511
[35]   Grain Boundary Character and Microstructural Evolution During Hot Deformation of a High Nb Containing TiAI Alloy [J].
Zhao Ruifeng ;
Zhou Huan ;
Zhang Tiebang ;
Kou Hongchao ;
Li Jinshan .
RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (10) :2927-2935
[36]   Grain boundary engineering for intergranular corrosion resistant austenitic stainless steel [J].
Kokawa, H ;
Shimada, M ;
Wang, ZJ ;
Sato, YS ;
Michiuchi, M .
ADVANCES IN FRACTURE AND FAILURE PREVENTION, PTS 1 AND 2, 2004, 261-263 :1005-1010
[37]   THE INFLUENCE OF THE STARTING GRAIN SIZE DURING HIGH-TEMPERATURE GRAIN BOUNDARY ENGINEERING OF Ni-BASE SUPERALLOY RR1000 [J].
Detrois, Martin ;
Rotella, John ;
Goetz, Robert L. ;
Helmink, Randolph C. ;
Tin, Sammy .
PROCEEDINGS OF THE 13TH INTENATIONAL SYMPOSIUM OF SUPERALLOYS (SUPERALLOYS 2016), 2016, :459-468
[38]   High-Temperature Air and Steam Oxidation and Oxide Layer Characteristics of Alloy 617 [J].
Archana, M. ;
Rao, Ch Jagadeeswara ;
Ningshen, S. ;
Philip, John .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2021, 30 (02) :931-943
[39]   High temperature corrosion behaviour of a gradient NiCoCrAlYSi coating II: Oxidation and hot corrosion [J].
Jiang, S. M. ;
Li, H. Q. ;
Ma, J. ;
Xu, C. Z. ;
Gong, J. ;
Sun, C. .
CORROSION SCIENCE, 2010, 52 (07) :2316-2322
[40]   Effect of grain boundary engineering on electrochemical and intergranular corrosion of 316L stainless steel [J].
Wang, Chen ;
Yin, Jun ;
He, Jiayi ;
Zhu, Xiaobo ;
Wu, Zikai ;
Luo, Kuangxin ;
Luo, Fenghua .
CORROSION SCIENCE, 2025, 254
12345