Effect of Na2SO4 and water vapor on the corrosion of Ti3SiC2

被引：15

作者：

Liu, Guangming

Li, Meishuan

Zhou, Yanchun

机构：

[1] Nanjing Inst Aeronaut Technol, Dept Mat Sci & Engn, Minist Educ, Key Lab Nondestruct Test, Nanchang 330034, Peoples R China

[2] Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China

来源：

OXIDATION OF METALS | 2006年 / 66卷 / 1-2期

关键词：

titanium-silicon carbide; corrosion; Na2SO4; water vapor;

D O I：

10.1007/s11085-006-9027-9

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The corrosion behavior of polycrystalline Ti3SiC2 was studied in the presence of Na2SO4 deposit and water vapor at 900 degrees C and 1000 degrees C. The mass gain per unit area of the samples superficially coated with Na2SO4 exposed to water vapor was slightly lower than that of the samples corroded without water vapor. The microstructure and composition of the scales were investigated by SEM/EDS and XRD. Pores were observed in the corroded sample surfaces. The main corrosion phases oil the sample surface were identified by XRD as TiO2, Na2Si2O5 and Na2TiO3. After Ti3SiC2 corroded in the presence of the Na2SO4 deposit and water vapor, the scale had a three-layer microstructure, which was different from the duplex corrosion scale formed on Ti3SiC2 beneath the Na2SO4 film without water vapor. Because water vapor penetrated the Corrosion layer and then reacted with SiO2 to form volatile Si(OH)(4), all intermediate porous and TiO2-enriched layer formed in the corrosion layer.

引用

页码：115 / 125

页数：11

共 22 条

[1] SYNTHESIS OF TITANIUM-SILICON CARBIDE [J].

ARUNAJATESAN, S ;

CARIM, AH .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1995, 78 (03) :667-672

[2]

Barin I., 1973, THERMOCHEMICAL PROPE

[3] Synthesis and characterization of a remarkable ceramic: Ti3SiC2 [J].

Barsoum, MW ;

ElRaghy, T .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1996, 79 (07) :1953-1956

[4] Experimental investigation and thermodynamic calculation of the titanium-silicon-carbon system [J].

Du, Y ;

Schuster, JC ;

Seifert, HJ ;

Aldinger, F .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2000, 83 (01) :197-203

[5] Dense Ti3SiC2 prepared by reactive HIP [J].

Gao, NF ;

Miyamoto, Y ;

Zhang, D .

JOURNAL OF MATERIALS SCIENCE, 1999, 34 (18) :4385-4392

[6]

HANCOCK P, 1990, WERKST KORROS, V41, P743

[7] HOT CORROSION OF SINTERED ALPHA-SIC AT 1000-DEGREES-C [J].

JACOBSON, NS ;

SMIALEK, JL .

JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1985, 68 (08) :432-439

[8]

Kofstad P., 1988, Elsevier Appl. Sci., V24, DOI [10.1002/crat.2170240408, DOI 10.1002/CRAT.2170240408]

[9] Influence of pre-oxidation on the hot corrosion of Ti3SiC2 in the mixture of Na2SO4-NaCl melts [J].

Liu, GM ;

Li, MS ;

Zhou, YC ;

Zhang, YM .

CORROSION SCIENCE, 2006, 48 (03) :650-661

[10] Hot corrosion of Ti3SiC2-based ceramics coated with Na2SO4 at 900 and 1000 °C in air [J].

Liu, GM ;

Li, MS ;

Zhou, YC .

CORROSION SCIENCE, 2003, 45 (06) :1217-1226

← 1 2 3 →