Studies on hot rolled galvanized steel sheets: Effect of reheating on galvanizing

被引：7

作者：

Chattopadhyay, A. ^{[1
,2
]}

Sarma, V. Subramanya ^{[2
]}

Murty, B. S. ^{[2
]}

Haldar, A. ^{[1
]}

Bhattacharjee, D. ^{[1
]}

机构：

[1] Tata Steel, Res & Dev, Jamshedpur 831007, Bihar, India

[2] Indian Inst Technol Madras, Dept Met & Mat Engn, Madras 600036, Tamil Nadu, India

来源：

SURFACE & COATINGS TECHNOLOGY | 2009年 / 203卷 / 22期

关键词：

Galvanizing; Hot rolled steel; Transmission electron microscopy (TEM); Heat treatment; Continuous annealing; ALLOYING ELEMENTS; INTERSTITIAL-FREE;

D O I：

10.1016/j.surfcoat.2009.05.005

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Galvanized hot rolled steel sheets are inferior to cold rolled sheets because of the segregation of carbides at the surface/sub-surface region. In order to change the distribution of the carbides at the surface/sub-surface region, continuous annealing/reheating operation is carried out at different temperatures prior to the galvanizing operation. The reheating temperature maintained in continuous annealing line is the main factor which redistributes the carbides at the surface/sub-surface region. At intercritical annealing temperature all the carbides get dissolved into the matrix and the surface became suitable for galvanizing reaction. The reducing atmosphere also plays an important role to remove all the room temperature oxides present at the surface. Thus, a combination of proper temperature and reducing atmosphere leads to the proper galvanizing on the hot rolled steel surface. (C) 2009 Elsevier B.V. All rights reserved.

引用

页码：3465 / 3471

页数：7

共 11 条

[1]

BORDIGNON L, 2001, 5 INT C ZINC ZINC AL, P19

[2] Studies on hot-rolled galvanized steel sheets: Segregation of alloying elements at the surface [J].

Chattopadhyay, A. ;

Sarma, V. Subramanya ;

Murty, B. S. ;

Haldar, A. ;

Bhattacharjee, D. .

SCRIPTA MATERIALIA, 2008, 59 (05) :522-525

[3]

CLAESSENS S, 2001, 5 INT C ZINC ZINC AL, P631

[4]

DEITS SH, 1990, ZINC-BASED STEEL COATING SYSTEMS : METALLURGY AND PERFORMANCE, P297

[5] Effect of the presence of alloying elements in interstitial-free and low-carbon steels on their surface composition after annealing in reducing atmospheres (dew point = -30°C) [J].

Feliu, S ;

Pérez-Revenga, ML .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (07) :2039-2050

[6] Influence of annealing conditions on the galvanizability and galvannealing properties of TiNb interstitial-free steels, strengthened with phosphorous and manganese [J].

Hertveldt, I ;

De Cooman, BC ;

Claessens, S .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2000, 31 (04) :1225-1232

[7]

HISAMATSU Y, 1989, SCI TECHNOLOGY ZINC, P3

[8] The effect of iron oxide as an inhibition layer on iron-zinc reactions during hot-dip galvanizing [J].

Jordan, CE ;

Marder, AR .

METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 1998, 29 (02) :479-484

[9]

Jyrkas K., 1996, Surface Engineering, V12, P68

[10] The metallurgy of zinc-coated steel [J].

Marder, AR .

PROGRESS IN MATERIALS SCIENCE, 2000, 45 (03) :191-271

← 1 2 →