Research on Dynamic Compression-Shear Behavior of Closed-Cell Aluminum Foam

被引：0

作者：

Lu, Jiangren ^{[1
]}

Zhang, Jian ^{[2
]}

Sun, Xinli ^{[1
]}

Cai, Xinghui ^{[1
]}

机构：

[1] Xian Res Inst Hitech Hongqing Town, Xian, Peoples R China

[2] Xi An Jiao Tong Univ, Sch Aerosp, Xian, Peoples R China

来源：

APPLIED MATERIALS AND TECHNOLOGIES FOR MODERN MANUFACTURING, PTS 1-4 | 2013年 / 423-426卷

关键词：

Closed-cell aluminum foam; Hopkinson pressure bar; Compression-shear; Strain rate effect;

D O I：

10.4028/www.scientific.net/AMM.423-426.1648

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this paper, the dynamic compression-shear experiments on the closed-cell aluminum foam with porosity of 72%-92% are carried out by using improved split Hopkinson pressure bar. A high speed camera is used to observe the dynamic deformation behavior of the samples on the compression-shear loading. A finite element software ABAQUS is employed to simulate the dynamic compression-shear process of closed-cell aluminum foam. The results demonstrate that there is a compression-shear band on the samples during the compression-shear loading. The most severely damaged area of the material is on the compression-shear band; Low-porosity closed-cell aluminum foam has significant strain rate effect, however high-porosity closed-cell aluminum foam can ignore the strain rate effect. The yield stress of samples decreases with increasing samples angle, whereas shear stress increase with increasing samples angle, and also the corresponding time when the samples just begin to yield decreases with increasing samples angle.

引用

页码：1648 / +

页数：2

共 5 条

[1]

Balch DK, 2005, MATER SCI ENG, V391

[2] Isotropic constitutive models for metallic foams [J].

Deshpande, VS ;

Fleck, NA .

JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 2000, 48 (6-7) :1253-1283

[3]

Gary G.T., 2000, American Society for Metals, V8, P462

[4] Dynamic indentation and penetration of aluminium foams [J].

Lu, G. ;

Shen, J. ;

Hou, W. ;

Ruan, D. ;

Ong, L. S. .

INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2008, 50 (05) :932-943

[5]

Zhao Wang-xiang, 2004, HEAT TREATMENT METAL, V29, P7

← 1 →