Carbide behavior during high temperature creep in DZ40M co-base superalloy

被引:0
作者
Jiang, WH [1 ]
Yao, XD [1 ]
Guan, HR [1 ]
Hu, ZQ [1 ]
机构
[1] Chinese Acad Sci, Inst Met Res, Shenyang 110015, Peoples R China
关键词
D O I
暂无
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The carbide behavior of a directionally solidified Co-base superalloy DZ40M has been investigated after creep at 700 degrees C and 900 degrees C. During the high temperature creep, a great amount of secondary carbide, M23C6 precipitated in alloy matrix. At 700 degrees C, the M23C6 precipitation occurred in slip bands, indicating that it was stress-induced, while at 900 degrees C, M23C6 formed surrounding the primary carbides, which is a characteristic of thermally aged alloy. The M23C6 particles pinned up dislocations and subgrain boundaries, strengthening the alloy matrix effectively. The creep crack initiation of DZ40M alloy was exclusively related to the primary carbides. The fracture of the primary carbide and the crack at the interface between them and matrix resulted in the crack formation. Furthermore, it was found that at 900 degrees C, the surface of specimens was oxidized severely and the preferentially oxidized primary carbides acted as crack initiation sites.
引用
收藏
页码:515 / 518
页数:4
相关论文
共 6 条
[1]  
GUAN HR, 1995, ACTA METALL SIN, V31, pS308
[2]   Secondary carbide precipitation in a directionally solidified cobalt-base superalloy [J].
Jiang, WH ;
Yao, XD ;
Guan, HR ;
Hu, ZQ .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (03) :513-520
[3]  
JIANG WH, 1998, ACTA METALL SINICA, V34, pA378
[4]  
SIMS CT, 1972, SUPERALLOYS, P154
[5]   LONG-TERM AGING CHARACTERISTICS OF HASTELLOY ALLOY-X [J].
TAWANCY, HM .
JOURNAL OF MATERIALS SCIENCE, 1983, 18 (10) :2976-2986
[6]  
Yao Xiangdong, 1995, Acta Metallurgica Sinica, V31, pA320