Effect of Air-Polishing on Titanium Surfaces, Biofilm Removal, and Biocompatibility: A Pilot Study

Purpose. The aims of this in vitro study were to evaluate morphological changes induced by glycine powder air-polishing on titanium surfaces, biofilm removal, and biocompatibility. Material and Methods. Titanium grade IV discs were allocated into two groups: (1) discs without biofilm and (2) discs for Streptococcus mutans biofilm formation. Discs in each group were further subdivided into (a) no treatment and (b) air-polishing treatment with glycine powder. Discs were characterized by scanning electron microscopy (SEM), electron-dispersive spectroscopy (EDS), and confocal microscopy. Bacterial biofilms were quantified using a crystal violet dye-binding assay. Biocompatibility was evaluated by measuring the coverage and viability of L929 fibroblast cells cultured on the discs. Results. Air-polishing increased the roughness of treated discs (p < 0.05). EDS analysis did not show significant differences in the chemical composition of treated and nontreated discs. The amount of residual biofilm on treated discs was 8.6-fold lower than untreated controls (p < 0.05). Coverage of treated discs by fibroblasts was half that of untreated discs (p < 0.05) although both groups had the same cell viability. Conclusions. Air-polishing removed a significant amount of biofilm from titanium surfaces. The "polishing" was accompanied by increased surface roughness, but there were no changes in chemical and elemental compositions, nor the biocompatibility.