Mechanical properties, corrosion behavior and microstructures of a non isothermal ageing treated Al-Zn-Mg-Cu alloy

被引:160
作者
Peng, Xiaoyan [1 ]
Guo, Qi [1 ]
Liang, Xiaopeng [1 ]
Deng, Ying [1 ]
Gu, Yi [1 ]
Xu, Guofu [1 ,2 ]
Yin, Zhimin [1 ]
机构
[1] Cent S Univ, Sch Mat Sci & Engn, Changsha 410083, Hunan, Peoples R China
[2] Minist Educ, Key Lab Nonferrous Mat Sci & Engn, Changsha 410083, Hunan, Peoples R China
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2017年 / 688卷
关键词
Al-Zn-Mg-Cu alloy; Non-isothermal ageing; Mechanical properties; Corrosion resistance; GRAIN-BOUNDARY SEGREGATION; 7050; ALUMINUM-ALLOY; ELECTROCHEMICAL-BEHAVIOR; PRECIPITATION BEHAVIOR; HEAT-TREATMENT; CRACKING; STRENGTH; RESISTANCE; RETROGRESSION; DIFFRACTION;
D O I
10.1016/j.msea.2017.01.086
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The mechanical properties, corrosion behavior, and microstructures of Al-Zn-Mg-Cu alloy during non isothermal ageing (NIA) process were investigated. The results suggest that hardness and tensile strength generally keep improving with increasing ageing degree until the level of 182 HV and 578 MPa (cooled at 120 degrees C, or C120), apart from a slight decline at the region where the temperature is beyond 200 degrees C. Synchronously, the electrical conductivity increases and corrosion susceptibility decreases as the ageing proceeds. The optimal performance of the alloy is obtained at the C120 condition, whose electrical conductivity, stress corrosion susceptibility r(tf) and maximum corrosion depth are 40.3 %IACS, 98.2% and 24.7 gm, respectively. GPI zones and eta' phases are the primary ageing precipitates at the heating stage (100-210 degrees C, 40 C/h), then eta' phases are the main ones at the cooling stage (210-100 degrees C, 20 C/h). Reasonably, the combination of high strength and favorable corrosion resistance of the alloy through NIA treatment are associated with the growth and coarsening of intergranular precipitates during heating and newly formed fine intragranular ones during cooling.
引用
收藏
页码:146 / 154
页数:9
相关论文
共 46 条
  • [1] GROWTH OF GRAIN BOUNDARY PRECIPITATES IN A1-4 PERCENT CU BY INTERFACIAL DIFFUSION
    AARON, HB
    AARONSON, HI
    [J]. ACTA METALLURGICA, 1968, 16 (06): : 789 - &
  • [2] [Anonymous], 79982005 GB
  • [3] GP-zones in Al-Zn-Mg alloys and their role in artificial aging
    Berg, LK
    Gjonnes, J
    Hansen, V
    Li, XZ
    Knutson-Wedel, M
    Waterloo, G
    Schryvers, D
    Wallenberg, LR
    [J]. ACTA MATERIALIA, 2001, 49 (17) : 3443 - 3451
  • [4] Effect of precipitate state on the stress corrosion behavior of 7050 aluminum alloy
    Chen, Junfeng
    Zhang, Xingfeng
    Zou, Linchi
    Yu, Yan
    Li, Qiang
    [J]. MATERIALS CHARACTERIZATION, 2016, 114 : 1 - 8
  • [5] Investigation of precipitation behavior and related hardening in AA 7055 aluminum alloy
    Chen, Junzhou
    Zhen, Liang
    Yang, Shoujie
    Shao, Wenzhu
    Dai, Shenglong
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 500 (1-2): : 34 - 42
  • [6] Effect of heat treatment on strength, exfoliation corrosion and electrochemical behavior of 7085 aluminum alloy
    Chen, Songyi
    Chen, Kanghua
    Peng, Guosheng
    Jia, Le
    Dong, Pengxuan
    [J]. MATERIALS & DESIGN, 2012, 35 : 93 - 98
  • [7] STRESS-CORROSION CRACKING OF AL-ZN-MG ALLOY AA-7039 BY SLOW STRAIN-RATE METHOD
    CHOI, Y
    KIM, HC
    PYUN, SI
    [J]. JOURNAL OF MATERIALS SCIENCE, 1984, 19 (05) : 1517 - 1521
  • [8] Cina B.M., 1974, US Patent, P12, Patent No. 3856584
  • [9] Effects of thermomechanical processing on production of Al-Zn-Mg-Cu alloy plate
    Deng, Yunlai
    Zhang, Yunya
    Wan, Li
    Zhang, Xinming
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 554 : 33 - 40
  • [10] A micromechanical method for predicting the precipitation hardening response of particle strengthened alloys hardened by ordered precipitates
    Fragomeni, JM
    Hillberry, BM
    [J]. ACTA MECHANICA, 1999, 138 (3-4) : 185 - 210