T6 Solutionizing Heat Treatment Parameter of A356 Alloy by Investment Casting

The heat treatment process is important to conduct on A356 Aluminum Alloy that broadly used in an automotive application. Analysis of the effect grain refinement, eutectic silicon modification of T6 solutionizing heat treatment parameter on strength development of A356 Aluminum Alloy were performed to become an important prospect of controlling the behaviour of materials as well as duration and temperature. In this study, there are three parameters condition were conducted which is duration Time (Hour) and Temperature (degrees C) which is 465 degrees C in 8 hours, 500 degrees C in 7 hours and 535 degrees C in 6 hours, respectively. The study generated three responses that are tensile, hardness test and microstructure analysis of the different temperature and duration time, respectively following by water-quenching. The result showed that the modification of duration time and high temperature of solutionizing heat treatment have superior mechanical properties while the microstructure analysis showed the clear formation of refinement alpha-Al dendrite and eutectic silicon particle.