Effect of Ce addition on microstructures and mechanical properties of A380 aluminum alloy prepared by squeeze-casting

被引：22

作者：

Ao, Xiao-hui ^{[1
]}

Xing, Shu-ming ^{[1
]}

Yu, Bai-shui ^{[1
]}

Han, Qing-you ^{[2
]}

机构：

[1] Beijing Jiaotong Univ, Sch Mech Elect & Control Engn, Beijing 100044, Peoples R China

[2] Purdue Univ, Dept Mech Engn, W Lafayette, IN 47907 USA

来源：

INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS | 2018年 / 25卷 / 05期

关键词：

cerium; eutectic Si; Fe-rich phases; squeeze-casting; mechanical properties; CONTAINING INTERMETALLIC COMPOUNDS; FE-RICH INTERMETALLICS; TENSILE PROPERTIES; IRON; BETA-AL5FESI; PHASES; CERIUM; NUCLEATION; PHOSPHORUS; BEHAVIOR;

D O I：

10.1007/s12613-018-1602-y

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effect of cerium (Ce) addition on the eutectic Si, beta-Al5FeSi phase, and the tensile properties of A380 alloy specimens prepared by squeeze-casting were studied by optical microscopy (OM), scanning electron microscopy (SEM), and X-ray diffraction (XRD). The experimental results showed that Ce more effectively modified the eutectic Si and refined the beta-Al5FeSi. The refinement effect significantly increased under a specific pressure of 100 MPa with the addition of Ce from 0.1wt% to 0.9wt%. In contrast, the average length and the aspect ratio of the eutectic Si and beta-Al5FeSi exhibited their optimal values when the content of the added Ce was greater than 0.5wt%. Needle-like Al8Cu4Ce was precipitated with the addition of excessive Ce; hence, the mechanical properties of A380 gradually decreased with increasing Ce content in the range from 0.3wt% to 0.9wt%.

引用

页码：554 / 563

页数：10

共 30 条

[1] Modification of Fe-containing intermetallic compounds by K addition to Fe-rich AA319 aluminum alloys
Ashtari, P
Tezuka, H
Sato, T
[J]. SCRIPTA MATERIALIA, 2005, 53 (08) : 937 - 942
[2] Influence of Li addition on intermetallic compound morphologies in Al-Si-Cu-Fe cast alloys
Ashtari, P
Tezuka, H
Sato, T
[J]. SCRIPTA MATERIALIA, 2004, 51 (01) : 43 - 46
[3] Discussion of "Effect of Strontium and Phosphorus on Eutectic Al-Si Nucleation and Formation of β-Al5FeSi in Hypoeutectic Al-Si Foundry Alloys"*
Campbell, John
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (05): : 1009 - 1010
[4] The nucleation of Fe-rich phases on oxide films in Al-11.5Si-0.4Mg cast alloys
Cao, X
Campbell, J
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2003, 34A (07): : 1409 - 1420
[5] As-cast morphology of iron-intermetallics in Al-Si foundry alloys
Dinnis, CM
Taylor, JA
Dahle, AK
[J]. SCRIPTA MATERIALIA, 2005, 53 (08) : 955 - 958
[6] Eidhed W, 2008, J MATER SCI TECHNOL, V24, P45
[7] Effects of La and Ce Addition on the Modification of Al-Si Based Alloys
Elgallad, Emad M.
Doty, Herbert W.
Alkahtani, Saleh A.
Samuel, Fawzy H.
[J]. ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2016, 2016
[8] Squeeze casting: an overview
Ghomashchi, MR
Vikhrov, A
[J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2000, 101 (1-3) : 1 - 9
[9] Effect of Ce and La on microstructure and properties of a 6xxx series type aluminum alloy
Hosseinifar, Mehdi
Malakhov, Dmitri V.
[J]. JOURNAL OF MATERIALS SCIENCE, 2008, 43 (22) : 7157 - 7164
[10] Effects of Ce, Mn, Cr on the Microstructure and Properties of High-iron Eutectic Al-Si Piston Alloy
Hu, Ping
Su, Yong
Chen, Wenping
Jiang, Yan
[J]. ADVANCES IN MATERIALS AND MATERIALS PROCESSING, PTS 1-3, 2013, 652-654 : 1023 - 1029

← 1 2 3 →