Antiferromagnetic resonance and phase diagrams of gadolinium ferroborate GdFe3(BO3)4

Antiferromagnetic resonance in single crystals of rhombohedral gadolinium ferroborate GdFe3(BO3)(4) was studied. The frequency-field dependences of antiferromagnetic resonance over the frequency range 26-70 GHz and the temperature dependences of resonance parameters for magnetic fields oriented along the crystal axis and in the basal plane were determined. It was found that the iron subsystem, which can be treated as a two-sublattice antiferromagnet with anisotropy of the easy-plane type, experienced ordering at T = 38 K. At temperatures below 20 K, the gadolinium subsystem with the opposite anisotropy sign strongly influenced the anisotropic properties of the crystal. This resulted in a spontaneous spin-reorientation transition from the easy-plane to the easy-axis state at 10 K. Below 10 K, magnetic field-induced transitions between the states were observed. Experimental phase diagrams on the temperature-magnetic field plane were constructed for fields oriented along the crystal axis and in the basal plane. A simple model was used to calculate the critical transition fields. The results were in close agreement with the experimental values measured at T = 4.2 K for both field orientations. (C) 2004 MAIK "Nauka / Interperiodica".