Mechanical properties and surface characteristics of an AA6060 alloy strained in tension at cryogenic and room temperature

被引:67
作者
Xu, Zebing [1 ]
Roven, Hans J. [1 ,2 ]
Jia, Zhihong [3 ]
机构
[1] Norwegian Univ Sci & Technol, Dept Mat Sci & Engn, N-7491 Trondheim, Norway
[2] Qatar Univ, Ctr Adv Mat, Doha, Qatar
[3] Chongqing Univ, Coll Mat Sci & Engn, Chongqing 400044, Peoples R China
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2015年 / 648卷
关键词
AA6060; alloy; Cryogenic temperature; Mechanical property; Surface characteristics; Homogenous deformation; SINGLE-CRYSTALS; ALUMINUM-ALLOY; SLIP SYSTEMS; ORIENTATION DEPENDENCE; PLASTIC-DEFORMATION; DISLOCATION-MOTION; AL; FRACTURE; BEHAVIOR; STRESS;
D O I
10.1016/j.msea.2015.09.083
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Mechanical properties at 77 K and 295 K and surface characteristics of an AA6060 alloy have been studied. The alloy exhibited significant differences in mechanical properties and fracture mechanisms at 77 K in comparison with that at 295 K. When the temperature decreases, the yield strength, the ultimate tensile strength and ductility to fracture are drastically increased from 217.2 MPa, 252.4 MPa, 14.5% to 251.6 MPa, 335.9 Mpa, 21.5% respectively, and the average diameter of dimples decreases from 8 gm to similar to 3 mu m. It is proposed that the changed behavior at cryogenic temperature can be attributed to an increased accumulation of dislocations at low temperature. Detailed inspections of the deformed polished sample surfaces show that slip localization in wide slip-bands is not promoted at 77 K, indicating that crystallographic slip is homogeneous, while activation of surface slip systems forming wide slip bands is much easier at 295 K and therefore the surfaces were deformed more in-homogeneously and localized. The homogeneity in slip behavior introduced more topography at 77 K than observed at 295 K and the enhanced topography might be due to more 3-dimensional (3D) lattice rotation in grains having a high Schmid factor, hence introducing more accumulation of local displacements in the thickness direction. (C) 2015 Elsevier B.V. All rights reserved.
引用
收藏
页码:350 / 358
页数:9
相关论文
共 44 条
[1]  
ABELL JS, 1971, J MATER SCI, V6, P361, DOI 10.1007/BF02403055
[2]   Effects of strain localization on surface roughening during sheet forming [J].
Becker, R .
ACTA MATERIALIA, 1998, 46 (04) :1385-1401
[3]   Features of the microstructure and low-temperature yield stress of quenched Al-Li alloys [J].
Braude, IS ;
Grigorova, TV ;
Isaev, NV ;
Pustovalov, VV ;
Fomenko, VS .
LOW TEMPERATURE PHYSICS, 2000, 26 (07) :529-533
[4]   Orientation dependence of slip band formation in single-crystal aluminum studied by photoelectron emission [J].
Cai, Mingdong ;
Langford, Stephen C. ;
Dickinson, J. Thomas .
ACTA MATERIALIA, 2008, 56 (20) :5938-5945
[5]   In-situ EBSD study of the active slip systems and lattice rotation behavior of surface grains in aluminum alloy during tensile deformation [J].
Chen, P. ;
Mao, S. C. ;
Liu, Y. ;
Wang, F. ;
Zhang, Y. F. ;
Zhang, Z. ;
Han, X. D. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 580 :114-124
[6]   The influence of microstructure on work hardening in aluminum [J].
Chu, D ;
Morris, JW .
ACTA MATERIALIA, 1996, 44 (07) :2599-2610
[7]  
Considere A., 1885, Annales des Ponts et Chaussees, V9, P574
[8]   Characterization of stress-strain relationships in Al over a wide range of testing temperatures [J].
Csanadi, Tamas ;
Chinh, Nguyen Q. ;
Gubicza, Jeno ;
Voeroes, Gyoergy ;
Langdon, Terence G. .
INTERNATIONAL JOURNAL OF PLASTICITY, 2014, 54 :178-192
[9]   Modeling of thermally activated dislocation glide and plastic flow through local obstacles [J].
Hiratani, M ;
Zbib, HM ;
Khaleel, MA .
INTERNATIONAL JOURNAL OF PLASTICITY, 2003, 19 (09) :1271-1296
[10]   Combined model of dislocation motion with thermally activated and drag-dependent stages [J].
Hiratani, M ;
Nadgorny, EM .
ACTA MATERIALIA, 2001, 49 (20) :4337-4346