Microstructural and tribological characterization of air plasma sprayed nanostructured alumina-titania coatings deposited with nitrogen and argon as primary plasma gases

被引：33
作者：
Bolleddu, V. [1 ]
Racherla, V. [1 ]
Bandyopadhyay, P. P. [1 ]
机构：
[1] Indian Inst Technol, Dept Mech Engn, Kharagpur 721302, W Bengal, India
来源：
MATERIALS & DESIGN | 2014年 / 59卷
关键词：
ABRASIVE WEAR CHARACTERISTICS; BEHAVIOR; PARAMETERS;
D O I：
10.1016/j.matdes.2014.02.040
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Air plasma sprayed nanostructured Al2O3-13wt%TiO2 coatings were deposited as a function of critical plasma spray parameter (CPSP), defined as the ratio of arc power to primary gas flow rate, using nitrogen and argon as the primary plasma gases. Microstructural features including percentage of alpha-Al2O3 phase, percentage of partially melted/unmelted regions, microhardness, and wear characteristics were evaluated for the deposited coatings. Effect of CPSP on microstructural and wear characteristics of coatings deposited with nitrogen was found to be relatively small. In contrast, significant effect of CPSP on coating characteristics was found for coatings deposited with argon. In wear tests, while strong effect of normal load on weight loss was observed for coatings deposited with nitrogen, weight loss for coatings deposited with argon was nearly independent of applied normal load, at least for coatings deposited at the highest CPSP. (C) 2014 Elsevier Ltd. All rights reserved.
引用
收藏
页码：252 / 263
页数：12
相关论文
共 21 条
[1]   CONTACT AND RUBBING OF FLAT SURFACES [J].
ARCHARD, JF .
JOURNAL OF APPLIED PHYSICS, 1953, 24 (08) :981-988
[2]   Wear behaviour of thermally sprayed ceramic oxide coatings [J].
Bolelli, Giovanni ;
Cannillo, Valeria ;
Lusvarghi, Luca ;
Manfredini, Tiziano .
WEAR, 2006, 261 (11-12) :1298-1315
[3]   Microstructural characterization of plasma sprayed conventional and nanostructured coatings with nitrogen as primary plasma gas [J].
Bolleddu, V. ;
Racherla, V. ;
Bandyopadhyay, P. P. .
SURFACE & COATINGS TECHNOLOGY, 2013, 235 :424-432
[4]   Effect of APS process parameters on wear behaviour of alumina-titania coatings [J].
Bounazef, M ;
Guessasma, S ;
Montavon, G ;
Coddet, C .
MATERIALS LETTERS, 2004, 58 (20) :2451-2455
[5]   Development and implementation of plasma sprayed nanostructured ceramic coatings [J].
Gell, M ;
Jordan, EH ;
Sohn, YH ;
Goberman, D ;
Shaw, L ;
Xiao, TD .
SURFACE & COATINGS TECHNOLOGY, 2001, 146 :48-54
[6]   Microstructure development of Al2O3-13wt.%TiO2 plasma sprayed coatings derived from nanocrystalline powders [J].
Goberman, D ;
Sohn, YH ;
Shaw, L ;
Jordan, E ;
Gell, M .
ACTA MATERIALIA, 2002, 50 (05) :1141-1152
[7]   Note on POD test parameters to study wear behaviour of alumina-titania coatings [J].
Guessasma, S ;
Bounazef, M ;
Coddet, C .
MATERIALS CHARACTERIZATION, 2004, 52 (03) :237-241
[8]   Investigation of nanostructured and conventional alumina-titania coatings prepared by air plasma spray process [J].
Ibrahim, A. ;
Hamid, Z. Abdel ;
Aal, A. Abdel .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (03) :663-668
[9]   Fabrication and evaluation of plasma sprayed nanostructured alumina-titania coatings with superior properties [J].
Jordan, EH ;
Gell, M ;
Sohn, YH ;
Goberman, D ;
Shaw, L ;
Jiang, S ;
Wang, M ;
Xiao, TD ;
Wang, Y ;
Strutt, P .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 301 (01) :80-89
[10]   Crystallization behaviors in the plasma-spheroidized alumina/zircon mixtures [J].
Khor, KA ;
Li, Y .
MATERIALS LETTERS, 2001, 48 (02) :57-63
123