Preparation and Characterization of Nanoporous Sodium Carboxymethyl Cellulose Hydrogel Beads

被引:85
作者
Akalin, Gulen Oytun [1 ]
Pulat, Mehlika [2 ]
机构
[1] Aksaray Univ, Sci & Technol Applicat & Res Ctr, TR-68000 Aksaray, Turkey
[2] Gazi Univ, Chem Dept, TR-06500 Ankara, Turkey
关键词
SWELLING BEHAVIOR; CONTROLLED-RELEASE; PH; DELIVERY; ACRYLAMIDE; ALGINATE; MICROSPHERES; CHITOSAN; SURFACE; ACID;
D O I
10.1155/2018/9676949
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
A series of nanoporous sodium carboxymethyl cellulose (NaCMC) hydrogel beads were prepared using FeCl3 ionic crosslinker by changing polymer and crosslinker percentages (%). Characteristics of the hydrogels were investigated by gel content, swelling test, degradation test, Attenuated Total Reflectance-Fourier Transform Infrared (ATR-FTIR), Scanning Electron Microscope/Energy Dispersive X-ray Analysis (SEM/EDX), and Atomic Force Microscopy (AFM). Swelling experiments were studied by changing time, temperature, and pH. The swelling percentage (S%) regularly decreased with increasing the amounts of polymer and crosslinker, in contrast with gel content results. NaCMC hydrogels were found to be sensitive to pH variations. The degradation test showed that hydrogels had good stability and their degradation period varied from 30 to 36 days. According to SEM analysis, NaCMC hydrogels had mostly nanoporous structure. The average granule and pore sizes of the least swollen NaCMC-12 hydrogel were found to be 13.1 +/- 0.3nm and 82.1 +/- 3.2 nm. The elemental compositions of hydrogels were determined with EDX. The minimum average surface roughness (R-a) and root mean square roughness (R-ms) parameters were found to be 15.7 +/- 1.9nm and 20.3 +/- 2.2nm for NaCMC-12 hydrogels by AFM. Due to their good morphologies, stabilities, and swelling behaviors, NaCMC hydrogels can be suitable for biomaterial applications.
引用
收藏
页数:12
相关论文
共 48 条
[1]  
Adel AM, 2010, J NAT SCI, V8, P8
[2]   Preparation of pH- and ionic-strength responsive biodegradable fumaric acid crosslinked carboxymethyl cellulose [J].
Akar, Emine ;
Altinisik, Aylin ;
Seki, Yoldas .
CARBOHYDRATE POLYMERS, 2012, 90 (04) :1634-1641
[3]  
Annabi N, 2010, TISSUE ENG PART B-RE, V16, P371, DOI 10.1089/ten.TEB.2009.0639
[4]   IMMOBILIZATION OF YEAST-CELLS IN ACRYLAMIDE-GEL MATRIX [J].
AYKUT, G ;
HASIRCI, VN ;
ALAEDDINOGLU, G .
BIOMATERIALS, 1988, 9 (02) :168-172
[5]   Swelling behavior of carboxymethylcellulose hydrogels in relation to cross-linking, pH, and charge density [J].
Barbucci, R ;
Magnani, A ;
Consumi, M .
MACROMOLECULES, 2000, 33 (20) :7475-7480
[6]   Synthesis of a novel supermagnetic iron oxide nanocomposite hydrogel based on graft copolymerization of poly((2-dimethylamino)ethyl methacrylate) onto salep for controlled release of drug [J].
Bardajee, Ghasem Rezanejade ;
Hooshyar, Zari ;
Asli, Maryam Jahanbakhsh ;
Shahidi, Fatemeh Emamjome ;
Dianatnejad, Nastaran .
MATERIALS SCIENCE AND ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2014, 36 :277-286
[7]   One-pot synthesis of biocompatible superparamagnetic iron oxide nanoparticles/hydrogel based on salep: Characterization and drug delivery [J].
Bardajee, Ghasem Rezanejade ;
Hooshyar, Zari .
CARBOHYDRATE POLYMERS, 2014, 101 :741-751
[8]   Novel nano-porous hydrogel as a carrier matrix for oral delivery of tetracycline hydrochloride [J].
Bardajee, Ghasem Rezanejade ;
Pourjavadi, Ali ;
Soleyman, Rouhollah .
COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2011, 392 (01) :16-24
[9]   5-fluorouracil release from copolymeric hydrogels of itaconic acid monoester .1. Acrylamide-co-monomethyl itaconate [J].
Blanco, MD ;
Garcia, O ;
Trigo, RM ;
Teijon, JM ;
Katime, I .
BIOMATERIALS, 1996, 17 (11) :1061-1067
[10]   Universal buffer soluttons and the association constant of veronal [J].
Britton, HTS ;
Robinson, RA .
JOURNAL OF THE CHEMICAL SOCIETY, 1931, :1456-1462