Adsorption and removal of arsenic (V) using crystalline manganese (II,III) oxide: Kinetics, equilibrium, effect of pH and ionic strength

Manganese (II,III) oxide (Mn3O4) crystalline powder was evaluated as a potential sorbent for removal of arsenic (V) from water. Adsorption isotherm experiments were carried out to determine the adsorption capacity using de-ionized (DI) water, a synthetic solution containing bicarbonate alkalinity, and two natual groundwater samples. Adsorption isotherm data followed the Langmuir and Freundlich equations, indicating favorable adsorption of arsenic (V) onto Mn3O4, while results from the Dubinin-Radushkevich equation were suggestive of chemisorption of arsenic (V). When normalized to the sorbent surface area, the maximum adsorption capacity of Mn3O4 for arsenic (V) was 101 mu g m(-2), comparable to that of activated alumina. Arsenic (V) adsorption onto Mn3O4 followed pseudo-second-order kinetics. Adsorption of arsenic (V) was greatest at pH 2, while adsorption at pH 7-9 was within 91% of maximum adsorption, whereas adsorption decreased to 32% of maximum adsorption at pH 10. Surface charge analysis confirmed the adsorption of arsenic (V) onto the acidic surface of the Mn3O4 sorbent with a pH(PZC) of 7.32. The presence of coexisting ions bicarbonate and phosphate resulted in a decrease in arsenic (V) uptake. Comparable adsorption capacities were obtained for the synthetic solution and both groundwater samples. Overall, crystalline Mn3O4 was an effective and viable sorbent for removal of arsenic (V) from natural water, removing greater than 95% of arsenic (V) from a 1 mg L-1 solution within 60 min of contact time.