Dynamics of ion bombardment-induced modifications of Si(001) at the radio-frequency-biased electrode in low-pressure oxygen plasmas:: In situ spectroscopic ellipsometry and Monte Carlo study

被引:3
作者
Amassian, A.
Svec, M.
Desjardins, P.
Martinu, L.
机构
[1] Ecole Polytech, Dept Engn Phys, Montreal, PQ H3C 3A7, Canada
[2] Ecole Polytech, RQMP, Montreal, PQ H3C 3A7, Canada
基金
加拿大自然科学与工程研究理事会;
关键词
D O I
10.1063/1.2337260
中图分类号
O59 [应用物理学];
学科分类号
摘要
Low-pressure O-2 plasma exposures were performed on c-Si(001) at a radio frequency (rf)-powered electrode in the presence of substrate self-biasing (V-B) from V-B=-60 to -600 V, in order to evaluate ion-surface interactions at the growth surface under ion bombardment conditions suitable for the fabrication of high quality optical coatings. The plasma-surface interactions were monitored in situ using real-time spectroscopic ellipsometry (RTSE), which reveals time- and ion-fluence-resolved information about depth-dependent modifications, such as damage and oxidation below the c-Si substrate surface. RTSE analysis indicates almost immediate damage formation (<< 1 s) to a depth of a few nanometers below the surface after exposure to a low oxygen ion fluence (similar to 5x10(14) O cm(-2)). Oxide growth is detected at intermediate fluence (similar to 10(15)-10(16) O cm(-2)) and is attributed to O subplantation (shallow implantation); it forms near the surface of the target on top of an O-deficient interfacial damage layer (DL). Both layers experience a self-limiting growth behavior at high fluence (> 10(17) cm(-2)) as oxide and DL thicknesses reach bias-dependent steady-state values, determined by the maximum ion penetration depth, which increases from similar to 3.6 to 9.5 nm for V-B=-60 to -600 V. The in situ experimental study was complemented by Monte Carlo TRIDYN simulations based on the binary collision approximation, which were modified to calculate dynamic changes in the composition of a target exposed to a broad-energy ion source (rf plasma source) at high fluence. Simulation results are found to agree exceptionally well with experiment. In addition, they reveal that the 1.2-3.5-nm-thick DL formed in the steady-state regime is a result of (1) damage formation due to the presence of a small number of high energy O+ ions in the plasma environment, capable of penetrating and damaging up to 3 nm deeper than the majority ion population (O-2(+)), and (2) because of important surface motion resulting from oxidation-induced swelling (at low fluence) and sputtering-induced recession (at high fluence). Surface motion in general is found to inhibit oxygen incorporation at high depth in the substrate, thus forming the O-deficient DL. We discuss the implications of these findings on optical coatings deposition and propose a growth mechanism for coatings subjected to intense ion bombardment. (c) 2006 American Institute of Physics.
引用
收藏
页数:16
相关论文
共 78 条
[21]   Implantation and damage under low-energy Si self-bombardment [J].
Hensel, H ;
Urbassek, HM .
PHYSICAL REVIEW B, 1998, 57 (08) :4756-4763
[22]   Ellipsometric determination of optical constants for silicon and thermally grown silicon dioxide via a multi-sample, multi-wavelength, multi-angle investigation [J].
Herzinger, CM ;
Johs, B ;
McGahan, WA ;
Woollam, JA ;
Paulson, W .
JOURNAL OF APPLIED PHYSICS, 1998, 83 (06) :3323-3336
[23]   Plasma assisted oxidation, anodization, and nitridation of silicon [J].
Hess, DW .
IBM JOURNAL OF RESEARCH AND DEVELOPMENT, 1999, 43 (1-2) :127-145
[24]   INSITU SPECTROSCOPIC ELLIPSOMETRY STUDY OF THE ELECTRON-CYCLOTRON RESONANCE PLASMA OXIDATION OF SILICON AND INTERFACIAL DAMAGE [J].
HU, YZ ;
JOSEPH, J ;
IRENE, EA .
APPLIED PHYSICS LETTERS, 1991, 59 (11) :1353-1355
[25]   APPLICATIONS OF SPECTROSCOPIC ELLIPSOMETRY TO MICROELECTRONICS [J].
IRENE, EA .
THIN SOLID FILMS, 1993, 233 (1-2) :96-111
[26]   Optical properties and color of hard quaternary nanocomposite TiCxNy/SiCN coatings prepared by plasma enhanced chemical vapor deposition [J].
Jedrzejowski, P ;
Klemberg-Sapieha, JE ;
Martinu, L .
SURFACE & COATINGS TECHNOLOGY, 2004, 188 :371-375
[27]   Optical characteristics and color of TiN/SiN1.3 nanocomposite coatings [J].
Jedrzejowski, P ;
Baloukas, B ;
Klemberg-Sapieha, JE ;
Martinu, L .
JOURNAL OF VACUUM SCIENCE & TECHNOLOGY A, 2004, 22 (03) :725-733
[28]   OPTICAL FUNCTIONS OF SILICON BETWEEN 1.7 AND 4.7 EV AT ELEVATED-TEMPERATURES [J].
JELLISON, GE ;
MODINE, FA .
PHYSICAL REVIEW B, 1983, 27 (12) :7466-7472
[29]  
Kaiser N., 2003, Optical interference coatings
[30]   THE DISPLACEMENT OF ATOMS IN SOLIDS BY RADIATION [J].
KINCHIN, GH ;
PEASE, RS .
REPORTS ON PROGRESS IN PHYSICS, 1955, 18 :1-51