Microstructural evolution during transient liquid phase bonding of Inconel 617 using Ni-Si-B filler metal

被引：75

作者：

Jalilian, F. ^{[1
]}

Jahazi, M. ^{[1
]}

Drew, R. A. L. ^{[1
]}

机构：

[1] McGill Univ, Dept Min Met & Mat Engn, Montreal, PQ H3A 2B2, Canada

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2006年 / 423卷 / 1-2期

关键词：

TLP bonding process; Inconel; 617; BNi-3; joint microstructure; borides; carbides;

D O I：

10.1016/j.msea.2006.02.030

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The influence of process parameters on microstructural characteristics of transient liquid phase (TLP) bonded Inconel 617 alloy was investigated. Experiments were carried out at 1065 degrees C using nickel based filler metal (Ni-4.5% Si-3% B) with B as the melting point depressant (MPD) element. Two different thickness of interlayer and various holding times were employed. The influence of these processing parameters on the characteristics of the joint area particularly size, morphology and composition of precipitates was investigated. The presence of MoB, Mo2B, M23C6, TiC, M23(B, C)(6) and Ni3B precipitates in the diffusion layer and Ni3B, Ni3Si and Ni5Si2 precipitates in the interlayer at the interface between the base metal and interlayer were demonstrated using electron back scattered diffraction (EBSD), energy dispersive spectrometry (EDS) and TEM. (c) 2006 Elsevier B.V. All rights reserved.

引用

页码：269 / 281

页数：13

共 28 条

[1] BALE CW, 2005, FACT
[2] Bassford T. H., 1979, APPL MAT PRESSURE VE, VMPC-10, P1
[3] TENSILE AND IMPACT PROPERTIES OF CANDIDATE ALLOYS FOR HIGH-TEMPERATURE GAS-COOLED REACTOR APPLICATIONS
BRUCH, U
SCHUHMACHER, D
ENNIS, PJ
TEHEESEN, E
[J]. NUCLEAR TECHNOLOGY, 1984, 66 (02) : 357 - 362
[4] DUALL DS, 1974, WELD J, V204, P203
[5] ELLIOTT RP, 1965, CONSTITUTION BINARY, P127
[6] EMILIANI M, 1988, THESIS BROWN U
[7] MICROSTRUCTURAL DEVELOPMENT IN TRANSIENT LIQUID-PHASE BONDING
GALE, WF
WALLACH, ER
[J]. METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (10): : 2451 - 2457
[8] PERFORMANCE OF INCONEL ALLOY 617 IN ACTUAL AND SIMULATED GAS-TURBINE ENVIRONMENTS
GANESAN, P
SMITH, GD
YATES, DH
[J]. MATERIALS AND MANUFACTURING PROCESSES, 1995, 10 (05) : 925 - 938
[9] GOLDSTEIN J, 2003, SCANNING ELECT MICRO, P278
[10] THE NONEQUILIBRIUM SEGREGATION OF BORON DURING THE RECRYSTALLIZATION OF NB-TREATED HSLA STEELS
HE, XL
DJAHAZI, M
JONAS, JJ
JACKMAN, J
[J]. ACTA METALLURGICA ET MATERIALIA, 1991, 39 (10): : 2295 - 2308

← 1 2 3 →