Phase transformation behavior of 3 mol% yttria partially-stabilized ZrO2 (3Y-PSZ) precursor powder by an isothermal method

被引:34
作者
Kuo, Chih-Wei [1 ]
Shen, Yun-Hwei [1 ]
Yen, Feng-Lin [2 ]
Cheng, Huy-Zu [3 ]
Hung, I-Ming [4 ]
Wen, Shaw-Bing [1 ]
Wang, Moo-Chin [2 ]
Stack, Margaret [5 ]
机构
[1] Natl Cheng Kung Univ, Dept Resources Engn, Tainan 70101, Taiwan
[2] Kaohsiung Med Univ, Dept Fragrance & Cosmet Sci, Kaohsiung 807, Taiwan
[3] I Shou Univ, Dept Mat Sci & Engn, Kaohsiung 84001, Taiwan
[4] Yuan Ze Univ, Dept Chem Engn & Mat Sci, Tao Yuan 320, Taiwan
[5] Univ Strathclyde, Dept Mech & Aerosp Engn, Glasgow, Lanark, Scotland
关键词
Phase transformation; Tetragonal ZrO2; Monoclinic ZrO2; 3 mol% yttria partially stabilized ZrO2 (3Y-PSZ); Martensitic transformation; METASTABLE TETRAGONAL ZIRCONIA; MONOCLINIC TRANSFORMATION; CRYSTALLIZATION KINETICS; MECHANISM; GROWTH; EQUILIBRIA; TRANSITION; CERAMICS; SIZE;
D O I
10.1016/j.ceramint.2013.09.112
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The phase transformation behavior of freeze-dried 3 mol% yttria-partially-stabilized zirconia (3Y-PSZ) precursor powder has been studied. When the freeze-dried 3Y-PSZ precursor powder was calcined at 773-1073 K for 2 h, the crystalline structure was composed of tetragonal and monoclinic ZrO2 as primary and secondary phases, respectively. The freeze-dried 3Y-PSZ precursor powder after calcination at 773 K, the monoclinic ZrO2 content abruptly increased from 8.00% to 31.51% and the tetragonal ZrO2 content suddenly decreased from 92.00% to 68.49%, with the duration increasing from 0.5 to 1 min. The activation energy of the isothermal transformation from tetragonal to monoclinic was 7.02 kJ/mol. The kinetics equation for the phase transformation from tetragonal to monoclinic in the freeze-dried 3Y-PSZ precursor powder between 773 K and 1273 K for various durations is described as ln(1/1-alpha) = 1/2.61[t(2.61)(1.50 x 10(-3))(2.61)exp(-7.02 x 10(3)/RT)]; whereas, the HRTEM image shows a typical monoclinic ZrO2 domain because of the stress-induced tetragonal to monoclinic ZrO2 martensitic transformation that has occurred. (C) 2013 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码:3243 / 3251
页数:9
相关论文
共 42 条
  • [1] Kinetics of phase change I - General theory
    Avrami, M
    [J]. JOURNAL OF CHEMICAL PHYSICS, 1939, 7 (12) : 1103 - 1112
  • [2] Chevalier J, 1999, J AM CERAM SOC, V82, P2150
  • [3] COHEN M, 1981, METALLURGICAL TREATI, P445
  • [4] PHASE-EQUILIBRIA AND IONIC-CONDUCTIVITY IN THE SYSTEM ZRO2-YB2O3-Y2O3
    CORMAN, GS
    STUBICAN, VS
    [J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1985, 68 (04) : 174 - 181
  • [5] CULLITY BD, 1967, ELEMENTS XRAY DIFFRA, P388
  • [6] HYDROTHERMAL CRYSTALLIZATION KINETICS OF META-ZRO2 AND T-ZRO2
    DENKEWICZ, RP
    TENHUISEN, KS
    ADAIR, JH
    [J]. JOURNAL OF MATERIALS RESEARCH, 1990, 5 (11) : 2698 - 2705
  • [7] Low-temperature ageing of zirconia-toughened alumina ceramics and its implication in biomedical implants
    Deville, S
    Chevalier, J
    Fantozzi, G
    Bartolomé, JF
    Requena, J
    Moya, JS
    Torrecillas, R
    Díaz, LA
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2003, 23 (15) : 2975 - 2982
  • [8] Crystallisation and sintering behaviour of nanocrystalline Y-TZP powders obtained by seeding-assisted chemical coprecipitation
    Durán, P
    Tartaj, J
    Fernández, JF
    Villegas, M
    Moure, C
    [J]. CERAMICS INTERNATIONAL, 1999, 25 (02) : 125 - 135
  • [10] STABILIZATION OF TETRAGONAL PHASE IN POLYCRYSTALLINE ZIRCONIA
    GUPTA, TK
    BECHTOLD, JH
    KUZNICKI, RC
    CADOFF, LH
    ROSSING, BR
    [J]. JOURNAL OF MATERIALS SCIENCE, 1977, 12 (12) : 2421 - 2426