Bond coat oxidation and its significance for life expectancy of thermal barrier coating systems

被引：42

作者：

Echsler, H ^{[1
]}

Renusch, D ^{[1
]}

Schütze, M ^{[1
]}

机构：

[1] DECHEMA EV, Karl Winnacker Inst, D-60486 Frankfurt, Germany

来源：

MATERIALS SCIENCE AND TECHNOLOGY | 2004年 / 20卷 / 03期

关键词：

thermal barrier coating; lifetime modelling; oxidation; physical defects;

D O I：

10.1179/026708304225012143

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The time and temperature dependent evolution of the microstructure of thermal barrier coating systems under isothermal conditions between 950 and 1100degreesC up to 5000 h are investigated for two APS - TBC systems and two EB-PVD systems. Kinetics for the thermally grown oxide thickness values, the beta phase depletion underneath the oxide scale and the physical defects in and around the thermally grown oxide are determined by extensive SEM and subsequent interactive image analysis. In the case of physical defects, the size of pores, interacting pore populations and maximum crack lengths are measured. Additionally, the latter are classified with respect to their local orientation in the thermally grown oxide or its vicinity. Finally, the results are discussed with regard to their significance in lifetime modelling of gas turbine components.

引用

页码：307 / 318

页数：12

共 13 条

[1]

Berghof-Hasselbächer E, 2003, PRAKT METALLOGR-PR M, V40, P219

[2] A mechanistic study of oxidation-induced degradation in a plasma-sprayed thermal barrier coating system. Part II: Life prediction model [J].

Busso, EP ;

Lin, J ;

Sakurai, S .

ACTA MATERIALIA, 2001, 49 (09) :1529-1536

[3]

DEMASI JT, 1989, 182230 CR NASA LEW R

[4]

ECHSLER H, 2002, P TURB S JUN BONN GE, P152

[5]

ECHSLER H, 2003, THESIS RWTH AACHEN

[6] ON THE MECHANICAL-BEHAVIOR OF BRITTLE COATINGS AND LAYERS [J].

EVANS, AG ;

CRUMLEY, GB ;

DEMARAY, RE .

OXIDATION OF METALS, 1983, 20 (5-6) :193-216

[7]

HANCOCK P, 1988, MATER SCI TECH SER, V4, P398, DOI 10.1179/026708388790331456

[8] Characterization of alumina scales formed during isothermal and cyclic oxidation of plasma-sprayed TBC systems at 1150°C [J].

Haynes, JA ;

Ferber, MK ;

Porter, WD ;

Rigney, ED .

OXIDATION OF METALS, 1999, 52 (1-2) :31-76

[9]

HERZOG R, 2001, P MAT WEEK 1 4 OCT M

[10]

MEIER SM, 1991, 189111 CR NASA LEW R

← 1 2 →