Influence of material models on the stress state in thermal barrier coating simulations

被引：24

作者：

Baeker, M. ^{[1
]}

机构：

[1] Tech Univ Carolo Wilhelmina Braunschweig, D-38106 Braunschweig, Germany

来源：

SURFACE & COATINGS TECHNOLOGY | 2014年 / 240卷

关键词：

Thermal barrier coating; Finite element modelling; Plasticity; Visco-plasticity; OXIDATION; SYSTEM; OXIDE; BEHAVIOR; CREEP;

D O I：

10.1016/j.surfcoat.2013.12.045

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The stress state and failure mechanisms of thermal barrier coating systems are frequently studied using finite element simulations. One problem in evaluating the results of such simulations is that the material behaviour of the top coat and especially of the thermally grown oxide is not well-known. Either plasticity or viscoplasticity is frequently assumed to be the dominating stress relaxation mechanism with the implicit assumption that both mechanisms will lead to similar stress patterns. In this contribution, this assumption is critically evaluated. Different combinations of plasticity or viscoplasticity for the top coat and the TGO are studied. If viscoplasticity is not present, the stress evolution is dominated by plastic ratchetting, but this is counteracted by creep relaxation if the creep strength is sufficiently low. (C) 2014 Elsevier B.V. All rights reserved.

引用

页码：301 / 310

页数：10

共 25 条

[1] Assessment of TBC systems failure mechanisms using a fracture mechanics approach [J].

Aktaa, J ;

Sfar, K ;

Munz, D .

ACTA MATERIALIA, 2005, 53 (16) :4399-4413

[2]

[Anonymous], 2011, HDB HOCHTEMPERATUR W, DOI DOI 10.1007/978-3-8348-9907-1

[3] The influence of axial loading on the interface stresses of thermal barrier coatings [J].

Baeker, M. ;

Roesler, J. ;

Affeldt, E. .

COMPUTATIONAL MATERIALS SCIENCE, 2009, 47 (02) :466-470

[4] Simulation of crack propagation in thermal barrier coatings with friction [J].

Baeker, Martin ;

Roesier, Joachim .

COMPUTATIONAL MATERIALS SCIENCE, 2012, 52 (01) :236-239

[5] A parametric study of the stress state of thermal barrier coatings Part II:: cooling stresses [J].

Bäker, M ;

Rösler, J ;

Heinze, G .

ACTA MATERIALIA, 2005, 53 (02) :469-476

[6]

Baker MH, 2012, RICHMOND THEATER FIRE: EARLY AMERICA'S FIRST GREAT DISASTER, P79

[7] Finite element analysis of stress distribution in thermal barrier coatings [J].

Bialas, Marcin .

SURFACE & COATINGS TECHNOLOGY, 2008, 202 (24) :6002-6010

[8] A mechanistic study of oxidation-induced degradation in a plasma-sprayed thermal barrier coating system. Part I: Model formulation [J].

Busso, EP ;

Lin, J ;

Sakurai, S ;

Nakayama, M .

ACTA MATERIALIA, 2001, 49 (09) :1515-1528

[9] Role of segregating dopants on the improved creep resistance of aluminum oxide [J].

Cho, J ;

Wang, CM ;

Chan, HM ;

Rickman, JM ;

Harmer, MP .

ACTA MATERIALIA, 1999, 47 (15-16) :4197-4207

[10] Mechanical behaviour of as sprayed and sintered air plasma sprayed partially stabilised zirconia [J].

Echsler, H ;

Renusch, D ;

Schütze, M .

MATERIALS SCIENCE AND TECHNOLOGY, 2004, 20 (07) :869-876

← 1 2 3 →