Microstructure and properties of MoSi2-MoB and MoSi2-Mo5Si3 molybdenum silicides

被引:43
作者
Schneibel, JH
Sekhar, JA
机构
[1] Oak Ridge Natl Lab, Div Met & Ceram, Oak Ridge, TN 37831 USA
[2] Micropyret Heaters Int Inc, Cincinnati, OH 45215 USA
[3] Univ Cincinnati, Cincinnati, OH 45221 USA
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2003年 / 340卷 / 1-2期
关键词
intermetallic; silicide; MoSi2; mechanical properties; oxidation;
D O I
10.1016/S0921-5093(02)00193-4
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
MoSi2-based intermetallics containing different volume fractions of MOB or Mo5Si3 were fabricated by hot-pressing MoSi2, MOB, and Mo5Si3 powders in vacuum. Both classes of alloys contained approximately 5 vol.% of dispersed silica phase. Additions of MoB or Mo5Si3 caused the average grain size to decrease. The decrease in the grain size was typically accompanied by an increase in flexure strength, a decrease in the room temperature fracture toughness, and a decrease in the hot strength (compressive creep strength) measured around 1200 degreesC, except when the Mo5Si3 effectively became the major phase. Oxidation measurements on the two classes of alloys were carried out in air. Both classes of alloys were protected from oxidation by an in-situ adherent scale that formed on exposure to high temperature. The scale, although not analyzed in detail, is commonly recognized in MoSi2 containing materials as consisting mostly of SiO2. The MOB containing materials showed an increase in the scale thickness and the cyclic oxidation rate at 1400 degreesC when compared with pure MoSi2. However, in contrast with the pure MoSi2 material, oxidation at 1400 degreesC began with a weight loss followed by a weight gain and the formation of the protective silica layer. The Mo5Si3 containing materials experienced substantial initial weight losses followed by regions of small weight changes. Overall, the MoB and Mo5Si3 additions to MoSi2 tended to be detrimental for the mechanical and oxidative properties. (C) 2002 Elsevier Science B.V. All rights reserved.
引用
收藏
页码:204 / 211
页数:8
相关论文
共 14 条
[1]  
BRADY MP, 2000, MAT SCI TECHNOLOGY, P229
[2]  
BROEK D, 1991, ELEMENTARY ENG FRACT
[3]  
Bundschuh K, 2001, MATER CORROS, V52, P268, DOI 10.1002/1521-4176(200104)52:4<268::AID-MACO268>3.0.CO
[4]  
2-C
[5]   Micropyretic synthesis of MoSi2 powders through an aluminothermic reaction [J].
Fu, M ;
Penumella, S ;
Sekhar, JA .
JOURNAL OF MATERIALS RESEARCH, 1999, 14 (05) :2023-2028
[6]   Development and characterization of SiC(f)/MoSi2-Si3N4(p) hybrid composites [J].
Hebsur, MG .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1999, 261 (1-2) :24-37
[7]   Compressive creep behavior of Mo5Si3 with the addition of boron [J].
Meyer, MK ;
Kramer, MJ ;
Akinca, M .
INTERMETALLICS, 1996, 4 (04) :273-281
[8]   Oxidation behavior of molybdenum silicides and their composites [J].
Natesan, K ;
Deevi, SC .
INTERMETALLICS, 2000, 8 (9-11) :1147-1158
[9]  
Nowotny H., 1957, MONATSH CHEM, V88, P180, DOI [10.1007/BF00901624, DOI 10.1007/BF00901624]
[10]   GRAIN-SIZE DEPENDENCE OF FRACTURE ENERGY IN CERAMICS .2. A MODEL FOR NONCUBIC MATERIALS [J].
RICE, RW ;
FREIMAN, SW .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1981, 64 (06) :350-354