Study of structural, electrical, magnetic and optical properties of 0.65BaTiO3-0.35Bi0.5Na0.5TiO3-BiFeO3 multiferroic composite

被引:61
作者
Rawat, Meera [1 ]
Yadav, K. L. [1 ]
机构
[1] Indian Inst Technol, Dept Phys, Smart Mat Res Lab, Roorkee 247667, Uttar Pradesh, India
关键词
Composite materials; Dielectric constant; Optical tuning; Magnetodielectric; Impedance analysis; FERROELECTRIC PROPERTIES; RESISTIVITY; CRYSTAL;
D O I
10.1016/j.jallcom.2014.01.059
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Conventional solid state reaction method was used to prepare (1 - x)[0.65BaTiO(3)-0.35Bi(0.5)Na(0.5)TiO(3)]xBiFeO(3) [where x = 0.0, 0.10, 0.15 and 0.20] composite. The presence of constituent phases in composite was confirmed by X-ray diffraction (XRD) studies. Average grain size was calculated by using field effect scanning electron microscope (FESEM) which increases from 356 nm to 577 nm with increase in ferrite content. Dielectric study confirms the presence of both ferroelectric and ferrite phases. We also found that the dielectric constant (epsilon) and Curie temperature (T-c) for ferrite phase increases with increase in the BiFeO3 content. Remnant polarization and coercive field for 0.65BaTiO(3)-0.35Bi(0.5)Na(0.5)TiO(3) are found to be 7.63 mu C/cm(2) and 9.55 kV/cm respectively, afterward these values decreases with increase in the ferrite content. Magnetic hysteresis were measured at temperature 300 K and 5 K using superconducting quantum interference device which shows that 0.65BaTiO(3)-0.35Bi(0.5)Na(0.5)TiO(3)-BiFeO3 has antiferromagnetic nature with unsaturated hysteresis loops so only able to obtain the magnetization (M-H) at 7 T. The antiferromagnetic nature of composite ceramics was also confirmed from the ZFC-FC curve. The presence of magnetocapacitance depicts the magnetoelectric coupling at room temperature. Impedance analysis provides the evidence of space charge accumulation in the samples, which vanish at higher frequencies and temperature. The electrical conductivity was observed to increase with rise in temperature which corresponds to the negative temperature coefficient of resistance (NTCR) behavior analogous to a semiconductor. Optical study shows that the band gap energies decrease with increase of BiFeO3 content. (C) 2014 Elsevier B. V. All rights reserved.
引用
收藏
页码:188 / 199
页数:12
相关论文
共 50 条
[41]   Structural and electromechanical properties of lead-free Na0.5Bi0.5TiO3-BaZrO3 ceramics [J].
Hussain, Ali ;
Rahman, Jamil Ur ;
Maqbool, Adnan ;
Kim, Min Su ;
Song, Tae Kwon ;
Kim, Won Jeong ;
Kim, Myong Ho .
PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE, 2014, 211 (08) :1704-1708
[42]   Phase Structure and Electrical Properties of Lead-Free (0.96Bi0.5Na0.5TiO3-0.04BaTiO3)-(0.98K0.5Na0.5NbO3-0.02LiTa03) Piezoelectric Ceramics [J].
Dai Yejing ;
Zhang Xiaowen .
RARE METAL MATERIALS AND ENGINEERING, 2009, 38 :282-285
[43]   Effects of Cobalt Dopant on Microstructure and Electrical Properties of Bi0.5Na0.5TiO3 Ceramics [J].
Buntham, Suwapitcha ;
Boonsong, Paitoon ;
Jaiban, Panupong ;
Keawprak, Nittaya ;
Watcharapasorn, Anucha .
CHIANG MAI JOURNAL OF SCIENCE, 2018, 45 (06) :2481-2490
[44]   High-Temperature Energy Storage Properties of Bi0.5Na0.5TiO3-0.06BaTiO3 Thin Films [J].
Alaoui, Ilham Hamdi ;
Lemee, Nathalie ;
Belhadi, Jamal ;
Le Marrec, Francoise ;
Cantaluppi, Anna ;
Lahmar, Abdelilah .
CRYSTALS, 2023, 13 (08)
[45]   Structure and Electrical Properties of Na0.5Bi0.5TiO3 Epitaxial Films with (110) Orientation [J].
Song, Jianmin ;
Gao, Jie ;
Zhang, Suwei ;
Luo, Laihui ;
Dai, Xiuhong ;
Zhao, Lei ;
Liu, Baoting .
CRYSTALS, 2019, 9 (11)
[46]   Electrical and luminescence properties of Er-doped Bi0.5Na0.5TiO3 ceramics [J].
Du, Peng ;
Luo, Laihui ;
Li, Weiping ;
Zhang, Yuepin ;
Chen, Hongbing .
MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2013, 178 (18) :1219-1223
[47]   Structure and multiferroic properties of ternary (1-x)(0.8BiFeO3-0.2BaTiO3) -xK0.5Na0.5NbO3 (0 ≤ x ≤ 0.5) solid solutions [J].
Zhou, S. D. ;
Wang, Y. G. ;
Li, Y. ;
Wu, H. ;
Zhu, L. .
CERAMICS INTERNATIONAL, 2019, 45 (06) :7210-7216
[48]   Impact of Gd3+ substitution on the structural, morphological, and electrical properties of lead-free Bi0.5Na0.5TiO3 ceramics [J].
Kuanar, Bijayalaxmi ;
Dalai, Biswajit ;
Behera, Dhrubananda ;
Mohanty, Hari Sankar .
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2023, 34 (06)
[49]   Tantalum doped 0-94Bi0.5Na0.5TiO3-0.06BaTiO3 piezoelectric ceramics [J].
Zuo, Ruzhong ;
Ye, Chun ;
Fang, Xusheng ;
Li, Jinwang .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2008, 28 (04) :871-877
[50]   Enhanced multiferroic properties of relaxor bulk and thin film Na0.5Bi0.5TiO3 by ion doping: Theoretical study [J].
Apostolova, I. N. ;
Apostolov, A. T. ;
Wesselinowa, J. M. .
SOLID STATE COMMUNICATIONS, 2021, 334